The invention relates to functional coating technology, aiming at providing a hard inorganic coating modified by nano SiO2 for coating valves. The coating is made up of the following raw material: silane coupling agent, KH570 10, 15, 10, 5, 3 silica sol, 40 silica sol 20, 10 nano alumina, 5 al Al2O3, 15 pigment of iron black pigment, 3 of organic acids, hydroxyl silicone oil and ethanol. The coating of the invention has strong adhesion, corrosion resistance and aging resistance and high hardness. The chemical bond can be formed with the base of the valve, so it has good adhesion. At the same time, the coating system is an inorganic system. After nanocomposite, the mechanical strength is much larger than the coating prepared by the existing coating, thus effectively prolonging the service life of the metal valve.
【技术实现步骤摘要】
用于涂覆阀门的纳米SiO2改性的硬质无机涂料
本专利技术涉及功能涂料
，具体而言，涉及一种用于涂覆阀门的纳米SiO2改性的硬质无机涂料。
技术介绍
阀门是流体输送系统中的控制部件，具有截止、调节、导流、防止逆流、稳压、分流或溢流泄压等功能。因此，喷涂在阀门表面的涂料必须具有耐水、耐冲击、耐热、隔热等性能，另一方面，阀门材料在使用过程中频繁发生摩擦，因此对于阀门的硬度要求较高，尤其是喷涂在金属阀门内部结构的涂料需要具备较强的防腐和抗老化性能以及耐磨性能。
技术实现思路
本专利技术要解决的技术问题是，克服现有技术中的不足，提供一种用于涂覆阀门的纳米SiO2改性的硬质无机涂料。该涂料附着力强、耐腐蚀、耐老化性能好，同时具有较高的硬度。为了实现上述目的，本专利技术所采用的技术方案为：提供一种用于涂覆阀门的纳米SiO2改性的硬质无机涂料及制备方法，该涂料是由以下重量份的原料组成的：硅烷偶联剂KH57010-15份、钛酸丁酯10-15份、水3-5份、二氧化硅溶胶20-40份、α纳米氧化铝10份、γ纳米氧化铝5份、铁黑颜料15-20份、有机酸3-5份、羟基硅油5-10份、乙醇...
【技术保护点】
一种用于涂覆阀门的纳米SiO2改性的硬质无机涂料，其特征在于，该涂料是由以下重量份的原料组成的：硅烷偶联剂KH570 10‑15份、钛酸丁酯10‑15份、水3‑5份、二氧化硅溶胶20‑40份、α纳米氧化铝10份、γ纳米氧化铝5份、铁黑颜料15‑20份、有机酸3‑5份、羟基硅油5‑10份、乙醇20份。
【技术特征摘要】
1.一种用于涂覆阀门的纳米SiO2改性的硬质无机涂料，其特征在于，该涂料是由以下重量份的原料组成的：硅烷偶联剂KH57010-15份、钛酸丁酯10-15份、水3-5份、二氧化硅溶胶20-40份、α纳米氧化铝10份、γ纳米氧化铝5份、铁黑颜料15-20份、有机酸3-5份、羟基硅油5-10份、乙醇20份。2.根据权利要求1所述的涂料，...