The present invention discloses a poly (lactic acid fiber) melt polypyrrole material, which consists of the following raw materials: 40 polylactic acid, 30 pyrrole, 0.7 chloride 0.8, linoleic acid 1 2, hydroxyethyl cellulose 5 7, benzo3 three nitroazole 0.8 2, lightweight calcium carbonate 6 6, single butyl oxide tin oxide, fatty acids. Poly (ethylene glycol) 1, 2, three ethylamine 2, 3. The acid doped polypyrrole solution of the invention can effectively improve the conductivity of polypyrrole by doping oleic acid. The blend of light calcium carbonate and amidation polylactic acid fiber can effectively achieve the compatibility of calcium carbonate, polylactic acid fiber and polypyrrole, thus improving the electrical conductivity and mechanical stability of the finished product.
【技术实现步骤摘要】
一种聚乳酸纤维熔融聚吡咯材料及其制备方法
本专利技术属于材料领域，具体涉及一种聚乳酸纤维熔融聚吡咯材料及其制备方法。
技术介绍
聚吡咯是化学中的专有名词，是常见黑色、不溶、不熔、导电的聚合物，聚吡咯通常通过吡咯单体氧化聚合得到，电化学阳极氧化吡咯也是制备聚吡咯的有效手段；聚吡咯可用于生物、离子检测、超电容及防静电材料及光电化学电池的修饰电极、蓄电池的电极材料。此外，还可以作为电磁屏蔽材料和气体分离膜材料，用于电解电容、电催化、导电聚合物复合材料等，应用范围很广，自从被发现以来一直受到人们的关注；然而导电聚吡咯材料的稳定性和力学性能差，为了改善和提高聚吡咯的性能，大量研究者将目光集中在聚吡咯与其他材料的复合上，近年来与碳纳米管等碳材料的复合广泛展开，研究结果表明与碳纳米管的复合能够大幅度的改善超级电容器的性能，然而碳纳米管有成本高、比电容低等缺点，因此本专利技术目的是研究一种全新的无机填料复合聚吡咯材料，以此来提高聚吡咯的稳定性强度和力学性能。
技术实现思路
本专利技术的目的在于针对现有技术的缺陷和不足，提供一种聚乳酸纤维熔融聚吡咯材料及其制备方法。为实现上述目的，本专...
【技术保护点】
一种聚乳酸纤维熔融聚吡咯材料，其特征在于，它是由下述重量份的原料组成的：聚乳酸40‑50、吡咯30‑37、三氯化铁0.7‑0.8、亚麻油酸1‑2、羟乙基纤维素5‑7、苯骈三氮唑0.8‑2、轻质碳酸钙6‑9、单丁基氧化锡0.4‑1、脂肪酸聚乙二醇酯1‑2、三乙胺2‑3。
【技术特征摘要】
1.一种聚乳酸纤维熔融聚吡咯材料，其特征在于，它是由下述重量份的原料组成的：聚乳酸40-50、吡咯30-37、三氯化铁0.7-0.8、亚麻油酸1-2、羟乙基纤维素5-7、苯骈三氮唑0.8-2、轻质碳酸钙6-9、单丁基氧化锡0.4-1、脂肪酸聚乙二醇酯1-2、三乙胺2-3。2.一种如权利要求1所述的聚乳酸纤维熔融聚吡咯材料的制备方法，其特征在于，包括以下步骤：(1)取羟乙基纤维素，加入到其重量14-20倍的去离子水中，升高温度为55-60℃，保温搅拌7-9分钟，得纤维溶液；(2)取苯骈三氮唑，加入到其重量3-5倍的无水乙醇中，升高温度为70-75℃，保温搅拌10-20分钟，得醇分散液；(3)取上述纤维溶液、醇分散液混合，搅拌均匀，加入三乙胺，超声1-2小时，蒸馏除去乙醇，得胺化纤维溶液；(4)取聚乳酸，加入到上述...