A kind of quantum functional fiber sheet, its raw material composition and weight share are: resin powder 33-58, wood powder 15-25, nanometer titanium dioxide 2-5, nano negative ion powder 3-15, foaming agent 0.5 - 2, coupling agent 1-2, active light calcium 10-20. The mixture of rice negative ion powder and some resin powder is mixed with coupling agent. Then the dried wood powder and the remaining resin powder are mixed with other raw materials to get the premixture. Then the extrusion premixture and the coextrusion premixture are added to the mixer to dehumidification, and the extruder is extruded in a screw extruder after cooling. Finally, it can be traced and cut. The design not only improves the effective life and purification effect of materials, but also improves the mechanical properties of materials.
【技术实现步骤摘要】
一种量子功能型纤维板材及其制备方法
本专利技术涉及木塑板材
，具体涉及一种量子功能型纤维板材及其制备方法。
技术介绍
木塑复合材料是以聚乙烯、聚丙烯、聚氯乙烯以及它们的共聚物等热塑性塑料和木粉为原料，经挤压、注塑、压制法成型所制成的复合材料。从生产原料来看，木塑复合材料的原料可以是各种回收利用的废旧塑料、废木料、农业废弃物等，因此其研制和广泛应用既有助于减缓塑料废弃物的公害污染，也利于减少农业废弃物焚烧给环境带来的污染。由于木塑复合材料的生产和使用不会向环境中释放有害物质，且材料本身还能回收再利用，因此属于一种绿色环保、生态洁净的复合材料。纳米负离子粉体是由天然矿物质材料通过纳米技术精心制成。科学研究表明，纳米负离子粉具有恒久的空气负离子发生功能、较强的远红外发射功能以及优良的抗菌杀菌功能，对人体保持精力充沛以及对人类居住环境的改善有极大的帮助作用，因此广泛应用于空气净化、保健以及水处理领域。目前，纳米负离子粉体多通过涂料喷洒或涂抹在板材表面的方式负载在木塑板材上，如中国专利申请公布号为CN104631769A、申请公布日为2015年5月20日的专利技术专利...
【技术保护点】
一种量子功能型纤维板材，其特征在于：所述板材的原料组成及其重量份数为：树脂粉33－58、木粉15－25、纳米二氧化钛2－5、纳米负离子粉体3－15、发泡剂0.5－2、偶联剂1－2、活性轻钙10－20。
【技术特征摘要】
1.一种量子功能型纤维板材，其特征在于：所述板材的原料组成及其重量份数为：树脂粉33－58、木粉15－25、纳米二氧化钛2－5、纳米负离子粉体3－15、发泡剂0.5－2、偶联剂1－2、活性轻钙10－20。2.根据权利要求1所述的一种量子功能型纤维板材，其特征在于：所述木粉由粒径均为80－120目、长径比均为1:2－4的竹粉、农作物秸秆粉以及杨木粉混合而成，且竹粉、农作物秸秆、杨木粉的重量份数比为1:2－3:2－3。3.根据权利要求1或2所述的一种量子功能型纤维板材，其特征在于：所述纳米负离子粉体为电气石、麦饭石、六环石纳米粉体中的至少一种。4.根据权利要求1或2所述的一种量子功能型纤维板材，其特征在于：所述板材的原料组成还包括重量份数为1－4的稳定剂和重量份数为1－5的调节剂。5.根据权利要求4所述的一种量子功能型纤维板材，其特征在于：所述发泡剂由AC和BHK-1组成，所述偶联剂为KH-570，所述稳定...
【专利技术属性】
技术研发人员：代祥云，金文准，
申请(专利权)人：湖北名望世家装饰材料股份有限公司，
类型：发明
国别省市：湖北,42
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。