The invention provides a sleeve grouting material, including the following components: 30 cement, 40 copies of sand 50, 1 portions of water reducing agent 5, 0.5 water retention agent 5, 1.5 parts 10.5 copies of early strength agent, 0.1 copies of super early strength agent, 3 copies of expansive agent, plastic expander, sodium rice enhancement agent, Xu Ning 0.1 doses of 0.5, 0.5 retarders, 0.5 defoamer and 0.1 carbonating agent 0.5, this slurry is about 20 degrees at room temperature, the flow degree can still remain above 300mm, 24h compressive strength can reach 50MPa, 3D compressive strength can reach 85MPa, 28d compressive strength can reach 120MPa, anti water shrinkage, carbonization shrinkage, body It has a slight expansibility, and the correlation is much higher than that of the same grouting material.
【技术实现步骤摘要】
一种套筒灌浆料
本专利技术涉及建筑材料
，具体涉及一种套筒灌浆料。
技术介绍
随着装配式建筑的发展，钢材连接件专用套筒灌浆料的使用会越来越普便，因为要在钢筋连接用套筒中起到连接作用，所以必须具有较高的抗压强度；普通灌浆料一般都会有收缩现像，钢筋连接用套筒灌浆料的膨胀率要求较高，借此增强与钢筋、套筒内侧间的正向作用力，钢筋即借由该正向力与粗糙表面产生的摩擦力，来传递钢筋应力钢材连接件专用套筒灌浆料一般要求较高的早期强度(24小时超过35MPa)、后期强度(28天超过85MPa)，流动度半小时要求较高，并且在如此大流动度的情况下体积收缩现像，而现有的同类灌浆料中，普遍流动性差，人工操性不强，特别是一天强度、三天强度匀不能达标，后期承受抗压强度小，并且28d天时体积有收缩现象，长时间甚至会致裂。
技术实现思路
为了解决上述技术问题，本专利技术提出了一种套筒灌浆料，包括以下组分：水泥30-50份、砂40份-50份、减水剂1份-5份、保水剂0.5-5份、早强剂1.5份-10.5份、超早强剂0.1份-0.6份、刚性膨胀剂3份-10份、塑性膨胀剂1份-3份、钠米增强剂3份-7...
【技术保护点】
一种套筒灌浆料，其特征在于，包括以下组分：水泥30‑50份、砂40份‑50份、减水剂1份‑5份、保水剂0.5‑5份、早强剂1.5份‑10.5份、超早强剂0.1份‑0.6份、刚性膨胀剂3份‑10份、塑性膨胀剂1份‑3份、钠米增强剂3份‑7份、絮凝剂0.1份‑0.5份、缓凝剂0.5份‑3份、消泡剂0.1份‑0.5份、抗碳化剂0.1份‑0.5份。
【技术特征摘要】
1.一种套筒灌浆料，其特征在于，包括以下组分：水泥30-50份、砂40份-50份、减水剂1份-5份、保水剂0.5-5份、早强剂1.5份-10.5份、超早强剂0.1份-0.6份、刚性膨胀剂3份-10份、塑性膨胀剂1份-3份、钠米增强剂3份-7份、絮凝剂0.1份-0.5份、缓凝剂0.5份-3份、消泡剂0.1份-0.5份、抗碳化剂0.1份-0.5份。2.根据权利要求1所述的套筒灌浆料...
【专利技术属性】
技术研发人员：李光球，陈集阳，翁小光，蔡志民，刘强，
申请(专利权)人：浙江共创建材科技有限公司，
类型：发明
国别省市：浙江,33