The invention relates to a wet mixed mortar admixture, which consists of a component of the following weight parts: 20 cellulose ether, 40 parts of sodium lignosulfonate, 30 copies of sodium lignosulfonate, 22 redispersible latex powder 14, 1.2 sodium twelve alkylbenzene 0.8, 0.6 gas entraining agent, 1 portion of air entraining agent and 900 1000 of fly ash 900. The invention has the advantages of the invention of wet mixed mortar admixture, in which the addition of cellulose ether has the effect of water retention and thickening; the air entraining agent can improve the mortars and the susceptibility to increase the yield of the mortar, and the formation of the mortar anti alkali can be prevented effectively by the fly ash as the filler, and the redispersible latex powder can be modified in the mortar. In addition, the use of sodium lignosulfonate water reducing agent can reduce the amount of water and increase the early strength of the mortar.
【技术实现步骤摘要】
一种湿拌砂浆外加剂
本专利技术属于建筑材料
，特别涉及一种湿拌砂浆外加剂。
技术介绍
近年来随着人们对环境问题关注度的日益提高，城市建设进程的加快，建设过程中产生的大量粉尘也成了城市环境污染物的主要来源之一。据统计，施工扬尘占城区粉尘排放量的23％，其中现场使用水泥、砂、石的粉尘排放量占施工扬尘总量的36％。传统的建筑砂浆在现场搅拌时，一般都没有封闭的作业现场，严重影响空气质量。特别是2013年以来全国大部分地区出现的雾霾天气，让人们重新对生态环境保护中的扬尘污染加以重视。相对于商品砂浆来说，现场搅拌砂浆也有大量的技术性缺点，比如砂浆施工性差、收缩率大、强度不稳定、抗渗性差等等问题。针对于以上出现的各类问题，各地政府也相继出台了以预拌砂浆取缔现场搅拌砂浆的文件。本专利技术就针对预拌砂浆中的湿拌砂浆而研发了一种湿拌砂浆所使用的外加剂。
技术实现思路
本专利技术要解决的技术问题是提供一种湿拌砂浆外加剂，以解决上述问题。为解决上述技术问题，本专利技术的技术方案为：一种湿拌砂浆外加剂，其创新点在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20-40份、木质素...
【技术保护点】
一种湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20‑40份、木质素磺酸钠20‑30份、可再分散性乳胶粉14‑22份、十二烷基苯黄酸钠0.8‑1.2份、引气剂0.6‑1.0份和粉煤灰900‑1000份。
【技术特征摘要】
1.一种湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20-40份、木质素磺酸钠20-30份、可再分散性乳胶粉14-22份、十二烷基苯黄酸钠0.8-1.2份、引气剂0.6-1.0份和粉煤灰900-1000份。2.根据权利要求1所述的湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚25-35...
【专利技术属性】
技术研发人员：耿晓滨，
申请(专利权)人：南通不二环境科技有限公司，
类型：发明
国别省市：江苏,32