The invention provides a method for reducing the production of iron water with two stages of reduction of complex refractory iron ore prereduction and reduction, which belongs to the non blast furnace ironmaking technology field. The method uses the complex refractory iron ore and non coking coal as raw material and mixed in a ring-shaped reheating furnace in proportion, and is heated to 750~1400, and stays for 1 to 10.0h. Original, then the reduced material was sent to the depth reduction furnace, the temperature was maintained at 1300~1500 degrees C, and the reduction process was 5 ~ 20.0h, and the iron metallization rate of the reduced iron water in the depth reduction furnace was over 95%.
【技术实现步骤摘要】
一种复杂难选铁矿预还原-再还原制取铁水的方法
本专利技术属于非高炉炼铁
，具体涉及一种复杂难选铁矿预还原-再还原制取铁水的方法。
技术介绍
我国复杂难选铁矿石储量超200亿吨，主要包括：鲕状赤铁矿石，微细粒赤铁矿石，难选镜铁矿石，褐铁矿石，菱铁矿石等类型铁矿石，由于以上类型铁矿石多嵌布粒度极细，矿物组成和矿石结构及构造复杂，采用常规的选矿方法难以选别富集，同时由于该类型铁矿石铁品位较低，杂质含量较多也无法实现直接冶炼生产铁水。因此在当前选矿、冶炼技术水平下，上述复杂难选铁矿石无法获得有效开发利用，导致我国不得不长期严重依赖国外进口铁矿石。目前国内铁矿石炼铁生产过程，通常采用选矿-烧结-球团-高炉炼铁的工艺流程，工艺流程复杂，生产中同时需要大量焦煤炼焦，导致该工艺流程投资大，能耗高，污染大。因此，取消当前炼铁过程中烧结-球团等高能耗高污染环节，实现我国难选铁矿石的资源化利用和非焦煤取代焦煤的利用，开发绿色高效短流程炼铁工艺技术，具有十分重要的经济效益和社会效益，同时有助于我国钢铁行业自主健康的可持续发展。
技术实现思路
本专利技术针对当前复杂难选铁矿石无法高效利用...
【技术保护点】
一种复杂难选铁矿预还原‑再还原制取铁水的方法，该方法以复杂难选铁矿石为原料，包括以下步骤：(1)原料选备，本方法选用铁矿石铁品位为25～55％，主要包括鲕状赤铁矿石、微细粒赤铁矿石、难选镜铁矿石、褐铁矿石、菱铁矿石和其他复杂难选的铁矿石为冶炼原料，选择固定碳含量≥70的各种类型非焦煤为还原剂；(2)原料破碎，将复杂难选铁矿石破碎至≤50mm，煤破碎至≤15mm；(3)原料混匀，按照重量比例配料混合，原料混合的重量比例为矿石:煤＝1:0.1～0.5；(4)将按比例混合后的原料送入环形加热炉内，在环形加热炉加热，在还原性气氛下进行预还原过程；环形加热炉内采用喷入煤粉、重油、煤气...
【技术特征摘要】
1.一种复杂难选铁矿预还原-再还原制取铁水的方法，该方法以复杂难选铁矿石为原料，包括以下步骤：(1)原料选备，本方法选用铁矿石铁品位为25～55％，主要包括鲕状赤铁矿石、微细粒赤铁矿石、难选镜铁矿石、褐铁矿石、菱铁矿石和其他复杂难选的铁矿石为冶炼原料，选择固定碳含量≥70的各种类型非焦煤为还原剂；(2)原料破碎，将复杂难选铁矿石破碎至≤50mm，煤破碎至≤15mm；(3)原料混匀，按照重量比例配料混合，原料混合的重量比例为矿石:煤＝1:0.1～0.5；(4)将按比例混合后的原料送入环形加热炉内，在环形加热炉加热，在还原性...
【专利技术属性】
技术研发人员：李艳军，袁帅，韩跃新，高鹏，孙永升，张淑敏，
申请(专利权)人：东北大学，
类型：发明
国别省市：辽宁,21