A method of two stage cascade reduction of iron ore with complex refractory iron ore, which belongs to the field of non blast furnace ironmaking, is characterized in that the complex refractory iron ore and non coking coal powder are used as raw materials to be mixed in a rotary kiln at 700~1300 degrees, and stay for 1 to 10.0h for a period of reduction, and then a section of reduction is made. The material is sent into the depth reduction furnace for 5 to 20.0h at 1100~1500 C, and the two section is reduced in depth. The iron metallization rate of the two reduced iron water discharged in the depth reduction furnace can be over 95%.
【技术实现步骤摘要】
一种难选铁矿石两段梯级还原生产铁水的新方法
本专利技术属于非高炉炼铁
，具体涉及一种复杂难选铁矿石采用预两段梯级还原工艺流程生产铁水的方法。
技术介绍
我国复杂难选铁矿石储量超200亿吨，主要包括：鲕状赤铁矿石，微细粒赤铁矿石，难选镜铁矿石，褐铁矿石，菱铁矿石等类型铁矿石，由于以上类型铁矿石多嵌布粒度极细，矿物组成和矿石结构及构造复杂,采用常规的选矿方法难以选别富集，同时由于该类型铁矿石铁品位较低，杂质含量较多也无法实现直接冶炼生产铁水。因此在当前选矿、冶炼技术水平下，上述复杂难选铁矿石无法获得有效开发利用，导致我国不得不长期严重依赖国外进口铁矿石。目前国内铁矿石炼铁生产过程，通常采用选矿-烧结-球团-高炉炼铁的工艺流程，工艺流程复杂，生产中同时需要大量焦煤炼焦，导致该工艺流程投资大，能耗高，污染大。因此，取消当前炼铁过程中烧结-球团等高能耗高污染环节，实现我国难选铁矿石的资源化利用和非焦煤取代焦煤的利用，开发绿色高效短流程炼铁工艺技术，具有十分重要的经济效益和社会效益，同时有助于我国钢铁行业自主健康的可持续发展。
技术实现思路
本专利技术针对当前复杂难选铁矿石...
【技术保护点】
一种复杂难选铁矿石两段梯级还原生产铁水的新方法，包括以下步骤：(1)原料选备，本方法选用铁矿石铁品位为25～55％，主要包括鲕状赤铁矿石、微细粒赤铁矿石、难选镜铁矿石、褐铁矿石、菱铁矿石和其他复杂难选的铁矿石为冶炼原料，选择固定碳含量≥70的各种类型非焦煤为还原剂；(2)原料破碎，将复杂难选铁矿石破碎至≤50mm，煤破碎至≤15mm；(3)原料混匀，按照重量比例配料混合获得混合物料，根据原料中铁矿物转变为Fe3O4所需要的碳含量计算，选择的的配煤过剩倍数为1.1～1.2；煤粉的配比量应保证在一次还原反应器内具有还原性氛围，并将反应器温度提高到所设计的温度，将矿石中的含铁矿物...
【技术特征摘要】
1.一种复杂难选铁矿石两段梯级还原生产铁水的新方法，包括以下步骤：(1)原料选备，本方法选用铁矿石铁品位为25～55％，主要包括鲕状赤铁矿石、微细粒赤铁矿石、难选镜铁矿石、褐铁矿石、菱铁矿石和其他复杂难选的铁矿石为冶炼原料，选择固定碳含量≥70的各种类型非焦煤为还原剂；(2)原料破碎，将复杂难选铁矿石破碎至≤50mm，煤破碎至≤15mm；(3)原料混匀，按照重量比例配料混合获得混合物料，根据原料中铁矿物转变为Fe3O4所需要的碳含量计算，选择的的配煤过剩倍数为1.1～1.2；煤粉的配比量应保证在一次还原反应器内具有还原性氛围，并将反应器温度提高到所设计的温度，将矿石中的含铁矿物还原成Fe3O4相态...