一种人造石用复合型固化剂及其制备方法技术

本发明专利技术公开了一种人造石用复合型固化剂，包括固化剂和溶剂，所述固化剂由TBPO、MEKP和TBPB组成，其中TBPB、TBPO、MEKP的摩尔比为1:(0.1‑0.4):0.5，所述固化剂的质量百分数为45％‑65％。本发明专利技术还公开了一种人造石用复合型固化剂的制备方法。本发明专利技术解决现有的三类固化剂的固化温度之外的固化聚合反应的同时可以解决固化剂常温下保存的问题。

Compound curing agent for artificial stone and preparation method thereof

The invention discloses a composite curing agent for artificial stone, including a curing agent and a solvent. The curing agent is composed of TBPO, MEKP and TBPB, in which the molar ratio of TBPB, TBPO and MEKP is 1: (0.1, 0.4): 0.5, and the mass percentage of the curing agent is 45% 65%. The invention also discloses a preparation method of compound curing agent for artificial stone. The present invention solves the problem of curing polymerization outside the curing temperature of the existing three kinds of curing agents and solves the problem of curing agent at normal temperature.

【技术实现步骤摘要】
一种人造石用复合型固化剂及其制备方法
本专利技术涉及人造石
，更具体地说，涉及一种人造石用复合型固化剂及其制备方法。
技术介绍
在建筑装磺装饰行业中，天然大理石曾以其高贵豪华而风靡于世界，但也存在以下不足和致命的弱点一是天然大理石属于一种矿产资源，其产地在世界上并不是很多，而且产量有限二是天然大理石刚度有余、强度不足，因此极易破碎、毁坏，造成了运输和日常维护的困难三是近年来科学研究发现，天然大理石具有一定的辐射性，会危害人体健康和污染环境。这些原因使其应用受到了很大的限制。所以，为了适应市场的需求和科学发展，人们将研究的方向转为利用废弃资源或其它低价原料，研制成本低、工艺简单的人造板材，即以一定的胶粘剂、外加剂及粗细骨料经一定工艺过程而制成的具有天然大理石花纹的装饰材料。坚实表面人造大理石(俗称人造石)自60年代在美国研制开发成功后，由于在卫生、款式、加工、美观(可实现无缝拼接)等方面具有天然大理石及其他材料无法比拟的优越性，因此一开始就受到市场关注。经过三十多年的发展和完善，已形成系列产品。按所用原材料树脂来区分的话，可分为以下二类：一类是以不饱和树脂(UPR)为粘接材料的人本文档来自技高网...

【技术保护点】
一种人造石用复合型固化剂，其特征在于，包括固化剂和溶剂，所述固化剂由TBPO、MEKP和TBPB组成，其中TBPB、TBPO、MEKP的摩尔比为1:(0.1‑0.4):0.5，所述固化剂的质量百分数为45％‑65％。

【技术特征摘要】
1.一种人造石用复合型固化剂，其特征在于，包括固化剂和溶剂，所述固化剂由TBPO、MEKP和TBPB组成，其中TBPB、TBPO、MEKP的摩尔比为1:(0.1-0.4):0.5，所述固化剂的质量百分数为45％-65％。2.如权利要求1所述的人造石用复合型固化剂，其特征在于，所述TBPB、TBPO、MEK...

【专利技术属性】
技术研发人员：方亨，韦杰，玉胜，
申请(专利权)人：方亨，
类型：发明
国别省市：广东,44