A high concentration formaldehyde urea formaldehyde resin preconditioning liquid synthesis process, characterized by the use of high concentration formaldehyde as the original, specific steps: raw materials according to the weight ratio, concentration of 50 formaldehyde 55% formaldehyde 30 35 copies, melamine 28 32 copies, caprolactam 1 3 copies, two glycoll 3, 4 copies, water 27 32 copies. The invention solves the problem of short storage period of urea formaldehyde resin Preshrinkage liquid produced by conventional methods, the subsequent process needs dehydration and the production of aldehyde containing wastewater, and provides a long storage period, and the subsequent use of urea formaldehyde resin with high concentration of formaldehyde Preshrinkage liquid with no dehydration.
【技术实现步骤摘要】
一种高浓度甲醛脲醛树脂预缩液合成工艺
本专利技术涉及人造板生产领域，尤其是高浓度甲醛预缩液的合成工艺。
技术介绍
浸渍三氰胶在常温下贮存3天以后，开始出现分层结晶，对生产组织和产品质量造成较大负面影响。浸渍三聚氰胺胶贮存稳定性是指由无色转变为乳白色的贮存时间，由于它属于初期树脂，性质极活泼，分子间易于相互结合，因为贮存时间短，如果继续缩聚，树脂粘度较高，渗透性、流展性差，达不到浸胶的使用要求。
技术实现思路
本法明的目的在于解决常规方法生产的脲醛树脂预缩液贮存期短，后续工艺需要脱水，产生含醛废水等问题，提供一种贮存期长，后续使用不需要脱水的脲醛树脂用高浓度甲醛预缩液合成工艺。本专利技术公开了一种高浓度甲醛脲醛树脂预缩液合成工艺，其特征在于使用高浓度甲醛作为原来，具体步骤为：原料按照重量分比，浓度50-55%甲醛30-35份，三聚氰胺28-32份，己内酰胺1-3份，二甘醇3-4份，水27-32份步骤1、在反应釜中依次加入甲醛、水25-30份，调节PH=9.0，投入二甘醇；步骤2、投入三聚氰胺、水2-3份；步骤3、开油在40～50Min内使反应液温度升至88.5℃，关油；...
【技术保护点】
一种高浓度甲醛脲醛树脂预缩液合成工艺，其特征在于使用高浓度甲醛作为原来，具体步骤为：原料按照重量分比，浓度50‑55%甲醛30‑35份，三聚氰胺28‑32份，己内酰胺1‑3份，二甘醇3‑4份，水27‑32份；步骤1、在反应釜中依次加入甲醛、水25‑30份，调节PH=9.0，投入二甘醇；步骤2、投入三聚氰胺、水2‑3份；步骤3、开油在40～50 Min内使反应液温度升至88.5℃，关油；步骤4、在88～89℃条件下保温60Min左右在冰水中出现雾点，投己内酰胺；步骤4、在20℃的水中检测水溶，当水溶至1.2倍时，开冷水降温；步骤5、调节PH=9.0，冷却至40℃以下放胶。
【技术特征摘要】
1.一种高浓度甲醛脲醛树脂预缩液合成工艺，其特征在于使用高浓度甲醛作为原来，具体步骤为：原料按照重量分比，浓度50-55%甲醛30-35份，三聚氰胺28-32份，己内酰胺1-3份，二甘醇3-4份，水27-32份；步骤1、在反应釜中依次加入甲醛、水25-30份，调节PH=9.0，投入二甘醇...
【专利技术属性】
技术研发人员：何云凯，徐立，毛顺国，储建基，郭兆辉，
申请(专利权)人：云南新泽兴人造板有限公司，
类型：发明
国别省市：云南,53