合金样件表面耐磨防护层的制备方法技术
Preparation of wear resistant protective coating on surface of alloy sample
The invention relates to a preparation method of a wear-resistant protective coating on the surface of an alloy sample. First, the alloy sample is treated by micro arc oxidation, a porous micro arc oxidation layer is obtained on the surface of the alloy sample, and a pore sealing agent is applied to the surface of the alloy sample. A self lubricating and wear-resistant coating composed of uniform micro arc oxidation layer and lubricating particle is prepared on the surface of alloy sample by micro arc oxidation and adding pore sealing agent, and the characteristics of organic combination of micropores and lubricating particles are effectively used to improve the corrosion resistance, wear resistance and lubricating properties of the alloy material.
【技术实现步骤摘要】
合金样件表面耐磨防护层的制备方法
本专利技术属于金属材料表面处理
，更具体地说，涉及合金样件表面耐磨防护层的制备方法。
技术介绍
金属材料因其较低的密度，良好的塑性、优良的导电性及导热性，在航空、航天、汽车、机械制造、船舶及化学工业中应用广泛。实际生产中，往往在机械强度满足要求的条件下使用铝、镁、钛等合金代替较重的钢材，从而减轻设备整体的重量，达到轻量化的目的。但是部分合金件易发生摩擦损伤、腐蚀和机械咬合现象，严重影响其正常使用，甚至引起器件和设备的功能性失效，因此，对合金进行表面处理是改善工件表面特性、延长其正常使用寿命的重要手段。通过微弧氧化技术可以在合金表面上原位生长硬质陶瓷层，使得基底金属和表面氧化陶瓷层完美结合，是一种较为理想的表面处理工艺。这层陶瓷膜具有优异的性能，包括高耐磨、耐腐蚀性、良好的高温稳定性及在相当宽的温度范围内具有较高的硬度，对于在高温和腐蚀介质中的摩擦情况下，其摩擦性能远比其他金属材料优异。虽然微弧氧化铝合金能在其表面形成较好的陶瓷保护层，但是不可避免的会存在许多孔洞或微裂纹，腐蚀介质通过这些缺陷渗入基体，导致其耐腐蚀性下降，破坏...
【技术保护点】
一种合金样件表面耐磨防护层的制备方法，其特征在于，包括如下步骤：（1）对合金样件进行微弧氧化处理，在合金样件表面获得多孔的微弧氧化层；（2）在步骤（1）处理后的合金样件表面施加封孔剂。
【技术特征摘要】
1.一种合金样件表面耐磨防护层的制备方法，其特征在于，包括如下步骤：（1）对合金样件进行微弧氧化处理，在合金样件表面获得多孔的微弧氧化层；（2）在步骤（1）处理后的合金样件表面施加封孔剂。2.根据权利要求1所述的合金样件表面耐磨防护层的制备方法，其特征在于，步骤（1）中，微弧氧化层上孔的孔隙直径范围在0~5μm之间，优选的，孔隙直径在1~5μm之间的孔占所有孔的20%~50%。3.根据权利要求1所述的合金样件表面耐磨防护层的制备方法，其特征在于，所述封孔剂中包含润滑颗粒，优选地，所述润滑颗粒的平均粒径与微弧氧化层表面孔隙平均直径之比在1/5~1/2之间，进一步优选地，所述润滑颗粒包括二硫化钼颗粒和/或石墨颗粒。4.根据权利要求3所述的合金样件表面耐磨防护层的制备方法，其特征在于，所述润滑颗粒的粒径选择范围在1~3μm。5.根据权利要求1所述的合金样件表面耐磨防护层的制备方法，其特征在于，所述...
【专利技术属性】
技术研发人员：邱从章，严雷鸣，黄娅婷，
申请(专利权)人：长沙新材料产业研究院有限公司，
类型：发明
国别省市：湖南,43