The invention discloses a water base cleaning agent for fouling aluminum and magnesium metal parts and the preparation method. The water base cleaning agent includes the following weight percentage of raw materials: OP 10, 0.8, 2.3%, alpha 0.3 sodium sulfonate 1%, propylene glycol butyl ether 0.08 0.35%, sodium citrate 0.3 1.5%, triethanolamine 0.2, 0.8%, D S 401 aluminum and die cast aluminum corrosion inhibitor 0.3 and 1.9%, deionized water 93 98%. The water base cleaning agent disclosed in the invention has strong penetration ability, can penetrate into the bottom of the cleaning material, quickly dissolve all kinds of dirt and impurities attached to the metal surface, without redeposition, cleaning process has no corrosion, no damage to the metal surface, clean speed, clean and bright metal surface after cleaning.
【技术实现步骤摘要】
一种用于污垢铝、镁金属件的水基清洗剂及其制备方法
本专利技术涉及一种用于污垢铝、镁金属件的水基清洗剂及其制备方法，尤其涉及一种用于ADC12铸铝合金废旧变速箱壳体的水基清洗剂及其制备方法。
技术介绍
汽车零部件再制造是指将废旧的零部件完全拆解、清洗、再加工、装配，并且通过测试恢复到具有原产品一样的技术性能和产品质量的生产工艺流程。在再制造过程中做好零件的清洗工作是保证再制造质量的重要一环，是对废旧零件进行鉴定、检测、加工、装配等工作的前提条件，对鉴定零件的准确性、保证再制造质量、降低再制造成本、提高再制造产品寿命等均能产生重要影响。目前市场上的很多水基清洗剂虽然也具有高效的去污能力，但是对于零部件大多具有一定的腐蚀性、且刺激性较大。
技术实现思路
基于以上背景，本专利技术提供了一种用于污垢铝、镁金属件的水基清洗剂及其制备方法。所述水基清洗剂可专门用于ADC12铸铝合金废旧变速箱壳体的清洗，能够有效去除油污、氧化物、以及汽车发动机运行过程中附着在零部件表面的其它物质形成的污垢。本专利技术采取的技术方案为：一种用于污垢铝、镁金属件的水基清洗剂，包括以下重量百分比的原料：O...
【技术保护点】
一种用于污垢铝、镁金属件的水基清洗剂，其特征在于，包括以下重量百分比的原料：OP‑10 0.8‑2.3％、α‑烯基磺酸钠0.3‑1.0％、丙二醇丁醚0.08‑0.35％、柠檬酸钠0.3‑1.5％、三乙醇胺0.2‑0.8％、DS‑401铝及压铸铝专用缓蚀剂0.3‑1.9％、去离子水93‑98％。
【技术特征摘要】
1.一种用于污垢铝、镁金属件的水基清洗剂，其特征在于，包括以下重量百分比的原料：OP-100.8-2.3％、α-烯基磺酸钠0.3-1.0％、丙二醇丁醚0.08-0.35％、柠檬酸钠0.3-1.5％、三乙醇胺0.2-0.8％、DS-401铝及压铸铝专用缓蚀剂0.3-1.9％、去离子水93-98％。2.根据权利要求1所述的水基清洗剂，其特征在于，包括以下重量百分比的原料：OP-101.5％、α-烯基磺酸钠0.8％、丙二醇丁醚0.3％、柠檬酸钠1.2％、三乙醇胺0.3％、DS-401铝及压铸铝专用缓蚀剂0.5％、去离子水95.4％。3.根据权利要求1或2所述的水基清洗剂的制备方法，其特征在于，包括以下步骤：(1)将配方量的α-烯基磺酸钠溶于部分蒸馏水中，搅拌使其全部溶解；(2)边搅拌边向步骤(1)中逐一加入配方量的...