The present invention relates to an ion exchange resin used for a terminal desalting high speed complex bed equipment. The preparation method of the ion exchange resin includes the following steps: quaternalization step: the quaternized reaction of chloromethylated polystyrene resin and alkyl guanidine in organic solvent to the chlorinated anion exchange resin; The procedure is to exchange the chloride ions in the resin with hydroxyl and obtain ion exchange resin. Compared with the conventional anion exchange resin, the ion exchange resin of the invention has better anti pollution ability and stability, more stable exchange capacity and longer service life.
【技术实现步骤摘要】
一种用于终端除盐高速复床设备的离子交换树脂及其制备方法
本专利技术涉及一种用于终端除盐高速复床设备的离子交换树脂，本专利技术还涉及一种用于终端除盐高速复床设备的离子交换树脂的制备方法。
技术介绍
近年来，随着亚临界、超临界、超超临界发电机组投入运行，对于锅炉补给水水质要求越来越高。在不锈钢冷轧生产过程中也需要用超纯水冲洗钢表面。半导体工业也特别需要超纯水。常用的超纯水制备方法有：离子交换法，一次蒸馏冷凝法，电渗析法等，目前主流工艺还是采用阳床+阴床+混床的离子交换处理工艺。阴床内装强碱性阴离子交换树脂，原水经过阴床，使水中的阴离子与离子交换树脂上的氢氧根离子发生反应，水中的各种阴离子被吸附在离子交换树脂上，而离子交换树脂上的氢氧根离子则到了水中，达到脱除杂质阴离子的目的。但是常规离子交换树脂稳定性及抗有机物污染性差，常规离子交换树脂通常适用于30℃-60℃，原水中的各种有机物会妨碍离子交换树脂的效果，虽然采用氢氧化钠再生时，有一部分有机物会清洗出来，但是仍然有相当数量的有机物不能克服范德华力而继续留在树脂内部。受污染的树脂因为交换容量下降会造成再生用水量升高同时制...
【技术保护点】
一种用于终端除盐高速复床设备的离子交换树脂， 其特征在于，所述离子交换树脂具有有以下结构通式：
【技术特征摘要】
1.一种用于终端除盐高速复床设备的离子交换树脂，其特征在于，所述离子交换树脂具有有以下结构通式：其中PS为聚苯乙烯共聚体树脂骨架，A+为烷基胍及其衍生物，具有以下的结构通式：其中，R1-R5可以独立地选自卤素、羟基、烷基中的一种或几种；B-为与树脂选用配对的阴离子。2.根据权利要求1所述的一种用于终端除盐高速复床设备的离子交换树脂，其特征在于，所述聚苯乙烯共聚体树脂为二乙烯基苯交联的聚苯乙烯共聚体树脂。3.根据权利要求1所述的一种用于终端除盐高速复床设备的离子交换树脂，其特征在于，所述聚苯乙烯共聚体树脂的交联度重量百分比为1-20%。4.一种用于终端除盐高速复床设备的离子交换树脂的制备方法，其特征在于，所述制备方法包括如下步骤：季铵化步骤：将氯甲基化聚苯乙烯树脂与烷基胍类化合物在有机溶剂中进行季铵化反应得到氯型阴离子交换树脂；转型处理步骤：用氢氧根将上述树脂中的氯离子交换，得到离子交换树脂。5.根据权利要求4所述的一种用于终端除盐高速复床设备的离子交换树脂的制备方法，其特征在于，所述烷基胍类化合物的结构如下：其中，R1-R5可以独立地选自卤素、羟基、烷基中的一种或几种；B为与树脂选用配对的阴离子。6.根据权利要求4所述的...
【专利技术属性】
技术研发人员：吴永琴，郑学勤，
申请(专利权)人：杭州浙源环境科技有限公司，
类型：发明
国别省市：浙江,33
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。