The present invention provides a method using red mud unburned ceramsite with red mud mixture, the preparation method comprises the following steps: (1) the red mud were dried to water content of less than 15%, iron ore to the mass fraction of Fe2O3 is less than or equal to 15%, and the removal of alkali treatment, the red mud pH 8~10 to pretreatment of red mud; (2) according to the ratio of weighing the raw materials, the raw materials for weight: pretreatment of red mud and fly ash 25~62 copies of 15~25 copies, 3~10 copies of the expanded perlite and clay 20~40; will call from the raw materials are mixed and evenly stirred, then grinding and sieving to obtain the red mud unburned ceramsite mixture. The invention fully exerts the characteristics of large specific surface area, strong alkalinity and certain gelling characteristics of red mud, effectively reduces the production cost of unburned ceramsite, and makes red mud and other industrial wastes to be reused, and has important economic and environmental benefits.
【技术实现步骤摘要】
一种免烧赤泥陶粒混合料及其制备方法
本专利技术属于有色冶金渣处理及资源化利用
，具体涉及一种利用氧化铝生产过程中产生的废渣赤泥生产免烧陶粒的方法。
技术介绍
氧化铝生产过程中排放的废渣是赤泥，其矿物组成主要有Al2O3、Na2O、SiO2、CaO、Fe2O3、TiO2等。赤泥主要有害成份是含有Na2O的附液，附液含碱2～3g/L，pH值在12.2～13.0之间，赤泥附液中含有Al2O3、Na2O、SiO2、CO2、NaCl、H2O等。河南三门峡某公司的赤泥化学成分见表1。表1赤泥主要化学成分表/％赤泥附液化学成分见表2。赤泥附液化学成分/(mg/L)(除pH)目前，赤泥的利用需要突破两个大的方向，一是低成本提取有价物质，二是降碱后将其用于混凝土等建筑材料。按照前期研究，含铁矿物随氧化铝变化，针铁矿、赤铁矿的比例也发生变化。样品矿物组成中赤铁矿含量在20-40％之间波动，针铁矿含量在18-27％之间波动，针铁矿为隐晶或微晶，多与其他矿物胶结，因此针铁矿含量的多少将在很大程度上影响精矿品位与回收率。另一方面，样品粒级细，比表面积大，且具有多孔结构。上述矿物中菱铁...
【技术保护点】
一种免烧赤泥陶粒混合料，各组分及其所占重量份数为：预处理赤泥25～62份、粉煤灰15～25份、膨胀珍珠岩3～10份、粘土20～40份。
【技术特征摘要】
1.一种免烧赤泥陶粒混合料，各组分及其所占重量份数为：预处理赤泥25～62份、粉煤灰15～25份、膨胀珍珠岩3～10份、粘土20～40份。2.根据权利要求1所述的免烧赤泥陶粒混合料，其特征在于，所述预处理赤泥由赤泥依次进行干燥至质量含水量≤15％，选铁至Fe2O3质量分数≤15％，并进行脱碱处理使其pH为8～10而成。3.根据权利要求1所述的免烧赤泥陶粒混合料，其特征在于，所述膨胀珍珠岩为膨胀珍珠岩砂，其密度小于100kg/m3，膨胀倍数大于10。4.根据权利要求1所述的免烧赤泥陶粒混合料，其特征在于，所述的粘土为废旧粘土质耐火...
【专利技术属性】
技术研发人员：李灿华，程勇，刘思，韩斌，何明生，倪俊，康凌晨，
申请(专利权)人：武汉钢铁有限公司，
类型：发明
国别省市：湖北,42