The invention discloses a shock resistant ceramic material and its preparation method, the impact resistance of ceramic materials, made comprises the following components by weight: silicon carbide 88 93 copies, 12 copies, 5 TiB2 fiber three two 5 7 antimony oxide, two phenyl methane diisocyanate 4 5, polyvinyl alcohol 2 3 copies, 3 copies, 2 barium carbonate were 2 3 copies, 1.5 copies, 0.5 copper oxide tartaric acid 0.5 1 and two (3, 5 three butyl 4 hydroxyphenyl) sulfide 0.05 0.9. The invention also provides a preparation method of impact resistance of ceramic materials, the method comprises the following steps: weighing the components are evenly mixed, heated to 500 DEG C 700, holding 1 2 hours, 10 ultrasound for 15 minutes, adding 1250 sintering kiln 1300 C 2 3H cooling. The impact resistance of ceramic materials.
【技术实现步骤摘要】
一种耐冲击陶瓷材料及其制备方法
本专利技术属于陶瓷材料领域，特别涉及一种耐冲击陶瓷材料及其制备方法。
技术介绍
陶瓷材料是用天然或合成化合物经过成形和高温烧结制成的一类无机非金属材料。根据陶瓷材料的用途可以将陶瓷材料分为普通陶瓷材料和特种陶瓷材料。陶瓷材料暗器性能又可分为高温陶瓷、超硬质陶瓷、高韧陶瓷、半导体陶瓷。电解质陶瓷、磁性陶瓷、导电性陶瓷等。随着成分、结构和工艺的不断改进，新型陶瓷层出不穷。因此制备得到的陶瓷材料也相应的具有特殊的力学、光、声、电、磁、热等性能，具有高熔点、高硬度、高耐磨性、耐氧化等优点。氮化硅高强度陶瓷以强度高著称，可用于制造燃气轮机的燃烧器、叶片、涡轮等。氨化硅陶瓷可代替金属制造发动机的耐热部件，能大幅度提高工件温度，从而提高热效率，降低燃料消耗，节约能源，减少发动机的体积和重量，而且又代替了如镍、铬、钠等重要金属材料。因此利用陶瓷的光学性能制造固体激光材料、光导纤维、光储存材料，以及陶瓷还用作压电材料、磁性材料、基底材料等。都证实了陶瓷材料有着广阔的应用前景。
技术实现思路
针对上述的需求，本专利技术特别提供了一种耐冲击陶瓷材料及其制备方...
【技术保护点】
一种耐冲击陶瓷材料，其特征在于，由包含以下重量份的组分制成：碳化硅 88‑93份,二硼化钛纤维 5‑12份,三氧化二锑 5‑7份，二苯基甲烷二异氰酸酯 4‑5份,聚乙烯醇 2‑3份,碳酸钡 2‑3份,三氧化钨 2‑3份,氧化铜 0.5‑1.5份,酒石酸 0.5‑1份,双(3，5‑三级丁基‑4‑羟基苯基)硫醚 0.05‑0.9份。
【技术特征摘要】
1.一种耐冲击陶瓷材料，其特征在于，由包含以下重量份的组分制成：碳化硅88-93份,二硼化钛纤维5-12份,三氧化二锑5-7份，二苯基甲烷二异氰酸酯4-5份,聚乙烯醇2-3份,碳酸钡2-3份,三氧化钨2-3份,氧化铜0.5-1.5份,酒石酸0.5-1份,双(3，5-三级丁基-4-羟基苯基)硫醚0.05-0.9份。2.根据权利要求1所述的耐冲击陶瓷材料，其特征在于，所述二硼化钛纤维的直径为20-35纳米。3.根据权利要求1所述的耐冲击陶瓷材料，其特征在于，所述聚乙烯醇的平均分子量为7500-8000。4.根据权利要求1所述的耐冲击陶瓷材料，其特征在于，所述组分还包括色粉0-0.5重量份。5.一种耐冲击陶瓷材料的制备方法，其特征在于，该方法包括以下步骤...
【专利技术属性】
技术研发人员：盖浩然，
申请(专利权)人：青岛东浩软件科技有限公司，
类型：发明
国别省市：山东,37