The invention discloses an acrylic anti-corrosion enamel, which belongs to the technical field of paint production. Acrylic anti-corrosive enamel of the invention, the composition comprises the following raw materials: acrylic resin, polyethylene glycol, filler, calcium propionate, leveling agent, dispersing agent, thickening agent, wetting agent, pigment, deionized water. The present invention is the preparation of acrylic enamel anti-corrosive acrylic resin, configuration, blending a series of steps. The invention of the acrylic anticorrosive enamel, wide source of raw materials, the ratio of science, has good antiseptic effect, as well as small, good anti friction or viscosity and anticorrosive advantages.
【技术实现步骤摘要】
一种丙烯酸防腐磁漆
本专利技术属于涂料生产
,具体涉及一种丙烯酸防腐磁漆。
技术介绍
丙烯酸漆具有极好的耐候性,很高的机械性能,是发展很快的一类涂料。丙烯酸漆可分为自干型丙烯酸漆(热塑型)和交联固化型丙烯酸漆(热固型),前者属于非转化型涂料,后者属于转化型涂料。自干型丙烯酸涂料主要用于建筑涂料、塑料涂料、电子涂料、道路划线涂料等,具有表干迅速、易于施工、保护和装饰作用明显的优点。缺点是固含量不容易太高,硬度、弹性不容易兼顾,一次施工不能得到很厚的涂膜,涂膜丰满性不够理想。交联固化型丙烯酸涂料主要有丙烯酸氨基漆、丙烯酸聚氨酯漆、丙烯酸醇酸漆、辐射固化丙烯酸涂料等品种。广泛用于汽车涂料、电器涂料、木器涂料、建筑涂料等方面。交联固化型丙烯酸涂料一般都具有很高的固含量,一次涂装可以得到很厚的涂膜,而且机械性能优良,可以制成高耐候性、高丰满度、高弹性、高硬度的涂料。缺点是双组分涂料,施工比较麻烦,许多品种还需要加热固化或辐射固化,对环境条件要求比较高,一般都需要较好的设备,较熟练的涂装技巧。丙烯酸磁漆是由丙烯酸树脂、加入各种颜料及增塑剂经研磨后加入有机溶剂配制而成。主要应用于磁器、瓷砖表面防护。近年来,随着消费者要求的不断提升,丙烯酸磁漆由于其成本低、防护力好、持久性好等优点,广受消费者喜欢。丙烯酸磁漆的相关配方技术也在不断发展。
技术实现思路
本专利技术提供了一种丙烯酸防腐磁漆,以解决现有丙烯酸磁漆持久性差、防腐性能不佳的问题。为解决以上技术问题,本专利技术采用以下技术方案:一种丙烯酸防腐磁漆,其组成以重量份为单位,包括以下原料:丙烯酸树脂30~45份、聚乙二醇 ...
【技术保护点】
一种丙烯酸防腐磁漆,其特征在于,该丙烯酸防腐磁漆的组成以重量份为单位,包括以下原料:丙烯酸树脂30~45份、聚乙二醇7~16份、填料12~22份、丙酸钙17~32份、流平剂3~11份、分散剂4~13份、增稠剂4~12份、润湿剂2.5~8.5份、颜料4~10份、去离子水45~60份。
【技术特征摘要】
1.一种丙烯酸防腐磁漆,其特征在于,该丙烯酸防腐磁漆的组成以重量份为单位,包括以下原料:丙烯酸树脂30~45份、聚乙二醇7~16份、填料12~22份、丙酸钙17~32份、流平剂3~11份、分散剂4~13份、增稠剂4~12份、润湿剂2.5~8.5份、颜料4~10份、去离子水45~60份。2.根据权利要求1所述的丙烯酸防腐磁漆,其特征在于,其制备方法包括以下步骤:将丙烯酸树脂加入反应釜中,再依次加入聚乙二醇、填料、丙酸钙、流平剂、分散剂、增稠...