The invention discloses a flame retardant sheath material used for wire and cable and a preparation method. One wire and cable for flame retardant sheath material, raw materials according to the following parts by weight: PVC resin 40 60 copies, 22 copies, 20 polyacrylate rubber 20 30 copies, 5 copies, 3 alumina glass fiber 10 15 copies, 4 plasticizer 6 copies, 15 copies of 10 TSP 0.5, stearic acid 1, 0.2 lubricants 0.5 copies, 8 copies of the 3 stabilizer and halogen-free flame retardant 3 8 copies, 4 copies, 2 wear-resisting agent processing agent 1 3. The sheath material produced by the invention has less smoke released during combustion, and greatly improves the resistivity and oxygen index, and effectively achieves the purposes of low smoke, low toxicity and flame retardancy.
【技术实现步骤摘要】
一种电线电缆用阻燃护套料及其制备方法
本专利技术属于电缆材料领域,具体涉及一种电线电缆用阻燃护套料及其制备方法。
技术介绍
PVC护套具有柔软、随意弯曲折叠、相对厚度薄、体积小、连接简单、拆卸方便等优点，可以任意选择导线数目及间距，使联线更方便，大大减少产品的体积，减少生产成本，提高生产效率，适合电器设备中作数据传输线缆或动力传输之用。而传统的PVC电缆护套由于自身配料不合理，致使制造成的护套抗拉强度较低，韧性差，在实际的使用过程中难免会将电缆弯曲或者扯拉，这样极易造成护套的破裂，无法继续对包裹在护套内部的电缆导体起到保护作用，使用寿命较短；电力电缆使用时一般都会在外层增加阻燃护套料，以防止电缆在积聚大量热量而发生火灾，而正是物料燃烧时产生的烟，这些烟不但产生大量的有毒物质，而且可以导致人窒息，这才是因火灾而死亡的主要因素，因此研究具有良好阻燃性能的电缆保护套是防止电力电缆火灾的重要课题。
技术实现思路
本专利技术提供了一种电线电缆用阻燃护套料及其制备方法，以解决上述技术问题。为了解决上述技术问题，本专利技术采用的技术方案是：一种电线电缆用阻燃护套料，由以下原料按重量...
【技术保护点】
一种电线电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：PVC树脂40‑60份、聚丙烯酸酯20‑22份、天然橡胶20‑30份、氧化铝3‑5份、玻璃纤维10‑15份、增塑剂4‑6份、重钙10‑15份、硬脂酸0.5‑1份、润滑剂0.2‑0.5份、稳定剂3‑8份、无卤阻燃剂3‑8份、耐磨剂2‑4份、加工助剂1‑3份。
【技术特征摘要】
1.一种电线电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：PVC树脂40-60份、聚丙烯酸酯20-22份、天然橡胶20-30份、氧化铝3-5份、玻璃纤维10-15份、增塑剂4-6份、重钙10-15份、硬脂酸0.5-1份、润滑剂0.2-0.5份、稳定剂3-8份、无卤阻燃剂3-8份、耐磨剂2-4份、加工助剂1-3份。2.根据权利要求1所述的电线电缆用阻燃护套料，其特征在于，由以下原料按重量份组成：PVC树脂50份、聚丙烯酸酯21份、天然橡胶25份、氧化铝4份、玻璃纤维1...
【专利技术属性】
技术研发人员：方文学，詹小兵，方揆民，李明，
申请(专利权)人：安徽万方管业集团有限公司，
类型：发明
国别省市：安徽,34