The invention discloses a preparation method of flame retardant plate, which is characterized in that the Magnesium Oxide adding copper sulfate solution, mix and stir for 20 minutes, the temperature was 40 degrees, and then adding expanded perlite and cement, with 320 RPM 10 stirring for 15 minutes, then add triethanolamine and stir for 10 minutes, add three chlorine fluoride methane, mixing, injection mould, the foam molding, curing, demoulding, cutting, flame retardant board is finished. The preparation method of the flame retardant plate has the advantages of low production cost and excellent water resistance. It is in accordance with the flame retardant standard GB8624 - 2006C grade and C class combustion grade.
【技术实现步骤摘要】
一种阻燃板的制备方法
本专利技术涉及一种建筑材料，特别涉及一种阻燃板的制备方法。
技术介绍
建筑及装饰行业非承重砌造产品采用的发泡水泥砖板、空心砖，比重大，隔音效果不佳；使用的硅酸钙板、石膏板，吸水性强易变形，经燃烧后强度不高易断裂，上述产品比重大，施工麻烦。泡沫板，则防火性能差，抗压强度不高。
技术实现思路
本专利技术针对上述问题提出了一种阻燃板的制备方法。具体的技术方案如下：一种阻燃板的制备方法，其特征在于，将氧化镁加入硫酸铜液，混合搅拌20分钟，温度为40度，再加入膨胀珍珠岩和水泥，以320转/分的转速搅拌10-15分钟，再加入三乙醇胺搅拌10分钟，添加三氯氟甲烷，搅拌均匀后，注入模具，经发泡成型、养护、脱模、切割等，即为成品阻燃板。上述一种阻燃板的制备方法，其特征在于，所述膨胀珍珠岩目数为500目。本专利技术的有益效果为：本专利技术阻燃板的制备方法制备得到的阻燃板生产成本低廉、耐水性能优异。符合阻燃标准GB8624—2006C级及C级以上燃烧等级。具体实施方式为使本专利技术的技术方案更加清晰明确，下面对本专利技术进行进一步描述，任何对本专利技术技术方案的技术特征进行等价替换和常规推理得出的方案均落入本专利技术保护范围。实施例1一种阻燃板的制备方法，其特征在于，制备方法如下：将25份氧化镁加入2份硫酸铜液，混合搅拌20分钟，温度为40度，再加入33份膨胀珍珠岩和1份水泥，以320转/分的转速搅拌10分钟，再加入4份三乙醇胺搅拌10分钟，添加3份三氯氟甲烷，搅拌均匀后，注入模具，经发泡成型、养护、脱模、切割等，即为成品阻燃板。实施例2一种阻燃板的制备方法，...
【技术保护点】
一种阻燃板的制备方法，其特征在于，将氧化镁加入硫酸铜液，混合搅拌20分钟，温度为40度，再加入膨胀珍珠岩和水泥，以320转/分的转速搅拌10‑15 分钟，再加入三乙醇胺搅拌10分钟，添加三氯氟甲烷，搅拌均匀后，注入模具，经发泡成型、养护、脱模、切割等，即为成品阻燃板。
【技术特征摘要】
1.一种阻燃板的制备方法，其特征在于，将氧化镁加入硫酸铜液，混合搅拌20分钟，温度为40度，再加入膨胀珍珠岩和水泥，以320转/分的转速搅拌10-15分钟，再加入三乙醇胺搅拌10...
【专利技术属性】
技术研发人员：吴江，陈秀兰，
申请(专利权)人：镇江泽枫霖建筑材料有限公司，
类型：发明
国别省市：江苏,32