The invention discloses a water bridge anti-corrosion coating, which is characterized in that comprises the following raw materials in weight portion: waterborne acrylic modified epoxy ester resin 50, 30 driers 0.3 0.6 copies, 0.4 copies, dispersant 760w0.2 substrate wetting agent BYK 0.3, pH 3480.1 regulator two monomethylethanolamine 1 3, defoamer BYK 240.1 0.3 copies, 25 copies, 2 pigment titanium dioxide 10 25 copies, 10 copies, 3 zinc phosphate anti rust agent 0.5 2 copies, 0.3 copies of 0.1 thickening agent and water 20 30. Water bridge anticorrosion coatings prepared by the invention, in order to ensure the salt fog resistance, water resistance, strong adhesion under the premise of volatile organic compounds in coatings decreased (VOC) content, so as to achieve a low environmental pollution, fire hazards of small effect, at the same time in the production and make any impact on the human body in the process of health will not.
【技术实现步骤摘要】
一种水性车桥防腐涂料
本专利技术涉及水性工业漆领域,尤其涉及一种车桥防腐涂料。
技术介绍
伴随着我国农业和汽车工业的发展,我国农用汽车行业销售额以每年10%-15%的速度增长。近年来,随着水性工业涂料的技术进步,水性工业涂料的应用取得快速发展,国内一些农机制造企业开始在农用汽车车桥上应用水性车桥防腐涂料替代溶剂型车桥防腐涂料。本专利技术水性车桥防腐涂料VOC释放量极低不仅解决了生产安全以及施工环保、健康等问题而且该产品施工适应性强,物化性能和工艺指标达到甚至超过同类型溶剂型产品的技术要求。
技术实现思路
本专利技术所要解决的技术问题是提供一种使用环保、生产安全的水性车桥防腐涂料。为实现上述目的,本专利技术采用的技术方案为:一种水性车桥防腐涂料,包括以下重量份的原料:水性丙烯酸改性环氧酯树脂30-50份、催干剂0.3-0.6份、分散剂760w0.2-0.4份、底材润湿剂BYK-3480.1-0.3份、pH调节剂二甲基乙醇胺1-3份、消泡剂BYK-0240.1-0.3份、颜料2-25份、二氧化钛10-25份、磷酸锌3-10份、防闪锈剂0.5-2份、增稠剂0.1-0.3份和水20-30份。作为优选,一种水性车桥防腐涂料,包括以下重量份的原料:水性丙烯酸改性环氧酯树脂38份、催干剂0.6份、分散剂760w0.3份、底材润湿剂BYK-3480.3份、pH调节剂二甲基乙醇胺1.6份、消泡剂BYK-0240.2份、颜料6份、二氧化钛25份、磷酸锌5份、防闪锈剂1份、增稠剂0.2份和水28份;其中所述颜料由以下重量份的原料组成:钛白粉R-8182.5份、酞青兰3.2份、永固紫 ...
【技术保护点】
一种水性车桥防腐涂料,其特征在于,包括以下重量份的原料:水性丙烯酸改性环氧酯树脂30‑50份、催干剂0.3‑0.6份、分散剂760w 0.2‑0.4份、底材润湿剂BYK‑348 0.1‑0.3份、pH调节剂二甲基乙醇胺1‑3份、消泡剂BYK‑024 0.1‑0.3份、颜料2‑25份、二氧化钛10‑25份、磷酸锌3‑10份、防闪锈剂0.5‑2份、增稠剂0.1‑0.3份和水20‑30份。
【技术特征摘要】
1.一种水性车桥防腐涂料,其特征在于,包括以下重量份的原料:水性丙烯酸改性环氧酯树脂30-50份、催干剂0.3-0.6份、分散剂760w0.2-0.4份、底材润湿剂BYK-3480.1-0.3...