A new type of rust coating applicable to the excavator's preparation method provided by the invention, by weight comprises the following components, waterborne acrylic modified epoxy resin 30 polyamide resin 20 90 copies, 60 copies, 5 copies of 3 zinc borate, epoxy soybean oil 2 6 copies, 1 barium carbide 3, polyisobutylene succinic imide two 4 8 copies, 4 copies of talcum powder 2, water 20 40, simple components, convenient configuration, low cost, no harm, rust and good performance, effectively avoid the influence of moisture in the air caused by the phenomenon of rust, drop phenomenon caused by excavator the surface coating, can effectively prolong the service life of the whole, time saving, low cost, can meet the needs of manufacturers.
【技术实现步骤摘要】
一种适用于挖土机的新型除锈涂料制备方法
本专利技术涉及涂料
，尤其涉及一种适用于挖土机的新型除锈涂料制备方法。
技术介绍
涂料，在中国传统名称为油漆。所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。然而现有的挖土机在长时间使用后，往往会受到空气中水汽的影响，在挖土机的表面会产生生锈的现象，造成挖土机表面涂料的掉落，需要定期的进行维护等工作，浪费大量的人力、物力，满足不了使用者的需求。
技术实现思路
本专利技术的目的是提供一种适用于挖土机的新型除锈涂料制备方法，解决现有的挖土机在长时间使用后，往往会受到空气中水汽的影响，在挖土机的表面会产生生锈的现象，造成挖土机表面涂料的掉落，需要定期的进行维护等工作，浪费大量的人力、物力，满足不了使用者的需求。本专利技术的目的可以通过以下技术方案实现；一种适用于挖土机的新型除锈涂料制备方法，其制备方法如下：（1）按重量份计称取以下组分,水性丙烯酸改性环氧树脂30-90份，聚酰胺树脂20-60份，硼...
【技术保护点】
一种适用于挖土机的新型除锈涂料制备方法，其特征为，其制备方法如下：（1）按重量份计称取以下组分, 水性丙烯酸改性环氧树脂30‑90份，聚酰胺树脂20‑60份，硼酸锌3‑5份，环氧大豆油2‑6份，碳化钡1‑3份，聚异丁烯丁二酰亚胺4‑8份，滑石粉2‑4份，水20‑40份；（2）将水性丙烯酸改性环氧树脂、聚酰胺树脂与水放入反应釜中，在30℃‑40℃下，均匀搅拌10‑20min；（3）当温度升至50℃‑60℃时，加入硼酸锌与碳化钡均匀搅拌10‑30min；（4）当温度升至65℃‑75℃时，加入聚异丁烯丁二酰亚胺与滑石粉，搅拌5‑15mim，当温度升至80℃‑100℃，加入环氧大豆...
【技术特征摘要】
1.一种适用于挖土机的新型除锈涂料制备方法，其特征为，其制备方法如下：（1）按重量份计称取以下组分,水性丙烯酸改性环氧树脂30-90份，聚酰胺树脂20-60份，硼酸锌3-5份，环氧大豆油2-6份，碳化钡1-3份，聚异丁烯丁二酰亚胺4-8份，滑石粉2-4份，水20-40份；（2）将水性丙烯酸改性环氧树脂、聚酰胺树脂与水放入反应釜中，在30℃-40℃下，均匀搅拌10-20min；（3）当温度升至50℃-60℃时，加入硼酸锌与碳化钡均匀搅拌10-30min；（4）当温度升至65℃-7...
【专利技术属性】
技术研发人员：蒋菊红，
申请(专利权)人：镇江兴润土石方工程有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。