一种铝合金用多元中间合金及其制备方法技术

本发明专利技术公开了一种铝合金用多元中间合金及其制备方法，所述多元中间合金质量组成为Mg 2～6％，Mn 0.2～0.8％，Sc 0.08～0.8％，Zr 0.08～0.4％，余量为Al；合金制备采用熔盐铝热还原法。本发明专利技术较大程度地减少了中间合金中钪锆的含量，提高了钪锆还原收得率，降低了含钪铝合金的生产成本；同时辅以镁锰强化，本发明专利技术的多元中间合金的综合性能良好，具有很好的强化变质效果。

A multi-element intermediate alloy for aluminum alloy and its preparation method

The invention discloses a preparation method of Aluminum Alloy with multiple intermediate alloy and process for the quality, the multiple intermediate alloy composed of Mg 2 ~ 6%, Mn 0.2 ~ 0.8%, 0.08 ~ 0.8% Sc, Zr 0.08 ~ 0.4%, the rest is Al; aluminum hot molten salt reduction method prepared by alloy. The invention greatly reduces the content of zirconium scandium alloy, scandium and zirconium increased yield reduction, reduced the production cost of SC Aluminum Alloy; at the same time with magnesium manganese enhanced, comprehensive performance of multiple intermediate alloy of the invention is good, have good enhancement modification effect.

【技术实现步骤摘要】
一种铝合金用多元中间合金及其制备方法
本专利技术涉及一种铝合金用多元中间合金及其制备方法，属于铝合金

技术介绍
航空航天、高铁及汽车的轻量化，极大推进变形铝合金的发展，轻质高强铝合金获得广泛应用。在变形铝合金材料的生产中，添加金属钪可以明显改善铝合金的性能，因此促进了钪在铝合金中的应用。由于钪的价格昂贵，钪的大量添加会使得铝合金的成本上升，因此一方面需要寻求代替金属钪的合金元素。中国专利技术专利公开了一种铝合金用的铝钪锆中间合金及其生产方法(申请号：2016103412981)，是用锆来代替部分钪，通过钪、锆来提高性能。钪锆等其他合金元素的加入方式通常以中间合金形式加入，如Al-Sc(Sc为2％)、Al-Zr(Zr为5％)中间合金，钪和锆均是铝合金强变质作用元素，其中钪是最好的变质元素，但成本高。在5系(Al-Mg)和7系(Al-Mg-Zn)铝合金中，用部分元素锆取代钪,钪锆复合添加变剂效果好、成本优。钪锆可以大幅度改善合金的屈服强度、焊接性能、耐蚀性能及加工性能。另一方面是降低铝钪中间合金的成本。在Al-Sc(2％)中间合金实际生产过程中，采用熔盐铝还原法，对于高含量钪合本文档来自技高网...

【技术保护点】
一种铝合金用多元中间合金，其特征在于，所述多元中间合金质量组成为Mg 2～6％，Mn 0.2～0.8％，Sc 0.08～0.8％，Zr 0.08～0.4％，余量为Al。

【技术特征摘要】
1.一种铝合金用多元中间合金，其特征在于，所述多元中间合金质量组成为Mg2～6％，Mn0.2～0.8％，Sc0.08～0.8％，Zr0.08～0.4％，余量为Al。2.一种权利要求1所述的多元中间合金的制备方法，其特征在于，包括以下步骤：(1)将质量比为100：1～7的纯Al和熔盐放入熔炼炉中，加热至熔化，并在850～980℃下，保温0.5-1小时；(2)降温至720～760℃，加入金属Mn和Mg，保温10-20分钟，搅拌使合金均匀化；(3)除去铝液表面熔盐，并在铝液中通入氩气，...

【专利技术属性】
技术研发人员：陈卫平，兰天翔，柳术平，王晓平，胡双，王力，
申请(专利权)人：湖南东方钪业股份有限公司，
类型：发明
国别省市：湖南,43