Titanium containing protecting furnace and the preparation method of the invention discloses a blast furnace, the grain size of titanium containing support for charge: 90% = 325 = 100%, 0 = 400 = 10%; comprises the following components: the mass percentage, including 52% ~ 55%, TiO2 from 30% to 32% TFe and a small amount of impurities; the impurities, including the mass percentage of < 2% SiO2, < content; 0.03% S, < content; 0.004% P, allowance for other impurities. The nurse in charge of titanium containing blast furnace by titanium furnace protecting process can be uniformly mixed with pulverized coal, fluidization velocity, and pulverized coal mixed in gas transmission process through no segregation phenomenon, greatly saves the BF furnace cost, with considerable economic benefits and value.
【技术实现步骤摘要】
一种高炉喷吹用含钛护炉料及其制备方法
本专利技术属于高炉护炉
，具体涉及一种利用炼铁高炉喷吹护炉时所用含钛护炉料及其制备方法，生产出一种适合高炉喷吹护炉用含钛护炉料。
技术介绍
高炉炉缸、炉底侵蚀是威胁高炉生产安全的重大隐患，同时是决定一代高炉寿命的主要因素。炉缸异常侵蚀在国内外高炉普遍存在，而有效控制高炉炉缸的异常侵蚀已成为世界炼铁工业的重要技术攻关目标。目前常规使用高炉加钛护炉的方法主要有两种，一种是从炉顶加入钛矿或含钛球团，一种是从风口喂线。这两种方法虽然都可以实现加钛护炉的目的，但都存在一定的缺陷。从炉顶加钛矿或含钛球团时，造成高炉生产指标下降，不利于高炉顺行。而从风口喂线护炉则需要专用的喂线设备，增加生产成本，同时喂线的过程也存在一定的安全隐患。中国专利CN102115798A提供了一种高喷煤配加钒钛矿粉喷吹护炉的方法，该方法将粉状钒钛物料连续、均匀的配加到原煤中，利用喷煤设施制粉及喷吹系统，通过煤粉输送管道，经煤粉分配器分配后，将粉状钒钛物料从高炉风口直吹管插入的喷煤枪喷入高炉炉缸。该方法部分地解决了由炉顶加钛矿和风口喂线护炉的缺陷，但也存在如下...
【技术保护点】
一种高炉喷吹用含钛护炉料，其特征在于，所述含钛护炉料的粒度级配为：90％≤‑325目≤100％，0≤‑400目≤10％；包括以下组分：以质量百分含量计,包括52％～55％的TiO2、30％～32％的TFe以及少量杂质；所述杂质中,包括质量百分含量<2.0％的SiO2、质量百分含量<0.03％的S、质量百分含量<0.004％的P，余量为其它杂质。
【技术特征摘要】
1.一种高炉喷吹用含钛护炉料，其特征在于，所述含钛护炉料的粒度级配为：90％≤-325目≤100％，0≤-400目≤10％；包括以下组分：以质量百分含量计,包括52％～55％的TiO2、30％～32％的TFe以及少量杂质；所述杂质中,包括质量百分含量<2.0％的SiO2、质量百分含量<0.03％的S、质量百分含量<0.004％的P，余量为其它杂质。2.根据权利要求1所述的高炉喷吹用含钛护炉料，其特征在于，包括以下组分：以质量百分含量计,包括53％～54％的TiO2、31％～32％的TFe以及少量杂质；所述杂质中,包括质量百分含量≤1.8％的SiO2、质量百分含量≤0.02％的S、质量百分含量≤0.035％的P，余量为其它杂质。3.根据权利要求1或2所述的高炉喷吹用含钛护炉料，其特征在于，所述含钛护炉料的粒度级配为-325目。4.制备权利要求1所述的高炉喷吹用含钛护炉料...
【专利技术属性】
技术研发人员：翟丹，金康，李实，
申请(专利权)人：翟丹，金康，李实，
类型：发明
国别省市：北京,11