The invention provides a highly dispersed graphene thermoplastic resin masterbatch, which is composed of Shi Moxi, carbon black, surfactant, auxiliaries, antioxidants, sulfonates, antiwear agents, extreme pressure agents: modifiers, hard ceramic particles and carrier resins. The raw material of the invention has the advantages of low cost, easy production, on the one hand can realize the charging performance of graphene effectively, at the same time makes graphene with self assembling by electrostatic, prevent graphene agglomeration, thereby greatly improving the stability of product quality and product performance, while effectively reduce the production the cost of raw materials, and helps overcome the production process caused by environmental pollution.
【技术实现步骤摘要】
一种高分散性石墨烯热塑性树脂母料
本专利技术涉及一种高分散性石墨烯热塑性树脂母料，属石墨烯化工
技术介绍
目前石墨烯树脂材料在当前的各行业中均有着极为广泛的应用，使用量巨大，但在实际使用中发现，当前的石墨烯树脂材料在生产和使用中，由于所采用的原料均为传统的原料配方，因此导致当前的石墨烯树脂往往存在结构强度和结构稳定性相对较差，且生产过程中存在较大物料浪费、生产效率相对较低且存在较大的环境污染现象，从而导致当前的石墨烯树脂材料生产制备效率和产品质量稳定性相对低下，且生产成本相对较高，于此同时，当前的石墨烯树脂材料在生产过程中，同时还不同程度存在石墨烯原料在树脂基材中的分散性相对较差，从而也导致石墨烯树脂材料成型性能较差，严重影响了石墨烯树脂材料的生产效率和质量，因此针对这一现状，需要开发一种全新的石墨烯树脂材料，以满足实际使用的需要。
技术实现思路
本专利技术的目的是提供本专利技术提供一种高分散性石墨烯热塑性树脂母料。为了达到上述目的，本专利技术提供如下技术方案：一种高分散性石墨烯热塑性树脂母料,由以下重量百分含量的组份构成：石墨烯：10%—55%；炭黑：3%...
【技术保护点】
一种高分散性石墨烯热塑性树脂母料, 其特征在于：所述的高分散性石墨烯热塑性树脂母料由以下重量百分含量的组份构成：石墨烯：10%—55%；炭黑：3%—18%；表面活性剂：0.1%—10%；助剂：0.1%—2%；抗氧化剂：0.1—3.5%；磺酸盐：0—3.3%；抗磨剂：2%—5%；极压剂：0.1%—0.5%；改性剂:0.2%—4.5%；硬质陶瓷颗粒：0.1%—3.5%；余量为载体树脂。
【技术特征摘要】
1.一种高分散性石墨烯热塑性树脂母料,其特征在于：所述的高分散性石墨烯热塑性树脂母料由以下重量百分含量的组份构成：石墨烯：10%—55%；炭黑：3%—18%；表面活性剂：0.1%—10%；助剂：0.1%—2%；抗氧化剂：0.1—3.5%；磺酸盐：0—3.3%；抗磨剂：2%—5%；极压剂：0.1%—0.5%；改性剂:0.2%—4.5%；硬质陶瓷颗粒：0.1%—3.5%；余量为载体树脂。2.根据权利要求1所述的一种高分散性石墨烯热塑性树脂母料，其特征在于：所述的石墨烯为高分子改性负载过渡金属络合物的石墨烯片层，且片层厚度为0.1—2.5nm。3.根据权利要求1所述的一种高分散性石墨烯热塑性树脂母料，其特征在于：所述的磺酸盐和硬质陶...
【专利技术属性】
技术研发人员：朱洋，邵蓉，
申请(专利权)人：南京旭羽睿材料科技有限公司，
类型：发明
国别省市：江苏,32