一种超快速制备Cu制造技术

本发明专利技术首次公开了一种超快速制备Cu

A method of super fast preparation of Cu2Se block thermoelectric materials

The invention discloses a method for rapid preparation of Cu2Se bulk thermoelectric materials, it uses Cu and Se powders as raw materials, the raw materials are mixed evenly, and then mixing the raw materials in graphite mold, placed in a plasma plasma activated sintering equipment in the sintering process of activation in plasma activation stage prepared by single phase dense Cu2Se bulk thermoelectric materials, the reaction synthesis and densification of Cu2Se compounds in one step. The invention relates to a process for the preparation of super simple, ultrashort time, the properties of Cu2Se bulk thermoelectric materials prepared by the superior, ZT> in the 773 range of 873K; 1.2, laid a good foundation for the large-scale preparation of Cu2Se compound preparation and application.

【技术实现步骤摘要】
一种超快速制备Cu2Se块体热电材料的方法
本专利技术属于热电材料制备
，具体涉及一种超快速制备Cu2Se块体热电材料的方法。
技术介绍
热电转换技术利用热电材料直接将热能与电能进行相互转换，具有系统体积小、可靠性高、不排放污染物质、适用温度范围广、有效利用低密度能量等特点，在工业余废热和汽车尾气废热的回收利用、高精度温控和特种电源技术等领域具有广泛的应用。热电材料的转换效率由无量纲热电优值ZT(ZT＝α2σT/κ，其中α为Seebeck系数、σ为电导率、κ为热导率、T为绝对温度)决定。ZT越大，材料的热电转换效率越高。目前研究较多的高性能热电材料一般是Te基的，如PbTe和Bi2Te3。Te元素在地球中的储量稀少、价格昂贵，同时它也是太阳能电池的主要组成元素，这些因素都极大地制约着Te基热电材料的大规模商业化应用和可持续性发展。因此开发储量丰富、价格低廉的高性能热电材料及寻求低成本超快速的制备方法具有重要意义。近年来Cu2Se化合物以其优异的热电性能受到研究者的广泛关注，因为其是典型的“声子液体”，表现出的横波阻尼效应使得其具有极低的晶格热导率。同时，由于Cu和Se的来源丰富本文档来自技高网...

【技术保护点】
一种超快速制备Cu2Se块体热电材料的方法，其特征在于，它以Cu粉和Se粉为原料，将原料混合均匀后，置于等离子体活化烧结设备中，在等离子体活化烧结工艺的等离子体活化阶段制备得到致密的Cu2Se块体热电材料。

【技术特征摘要】
1.一种超快速制备Cu2Se块体热电材料的方法，其特征在于，它以Cu粉和Se粉为原料，将原料混合均匀后，置于等离子体活化烧结设备中，在等离子体活化烧结工艺的等离子体活化阶段制备得到致密的Cu2Se块体热电材料。2.根据权利要求1所述的一种超快速制备Cu2Se块体热电材料的方法，其特征在于，所述等离子体活化阶段的时间为30-60s。3.根据权利要求1所述的一种超快速制备Cu2Se块体热电材料的方法，其特征在于，所述Cu粉和Se粉之间的摩尔比为(1.8-2):(1-1.1)。4.根据权利要...

【专利技术属性】
技术研发人员：唐新峰，杨东旺，唐贤贤，苏贤礼，鄢永高，
申请(专利权)人：武汉理工大学，
类型：发明
国别省市：湖北,42