The invention discloses a waterproof coating for textile, in accordance with the weight fraction comprises the following components: polyurethane resin 30 45 copies, 5 copies of 8 copies of coupling agent, crosslinking agent 6 12 copies, 5 copies of 15 copies of nanoparticle materials, solvent 12 15 copies, 0.4 copies of 1.2 pigment a defoamer, 1 3 copies, 5 copies of plasticizer 10, stabilizer 2 4; the solvent is a fluorinated solvent, the defoaming agent for silicone defoamer. By adding nanoparticle materials into the ingredients and using fluorinated solvents and organosilicon defoamers, we can ensure that the coatings at later stage can form a solid high density waterproof layer on the surface of fabrics.
【技术实现步骤摘要】
一种纺织用防水涂料
本专利技术涉及了一种纺织用防水涂料,属于纺织涂料
技术介绍
传统的防水面料长期处于潮湿的气候环境中能经得住渗水压力,不渗水,比如长时间地在风雨交加的户外行走,跪或坐在潮湿的地面,都不会渗水。在防水面料的生产过程中,通常在面料的表面加工一层防水涂层,利用防水涂层的防水性使面料具有防水的功能。但是现有的防水涂料通常防水性不稳定,在长时间使用后会逐渐丧失防水性能。
技术实现思路
本专利技术所要解决的技术问题是提供一种纺织用防水涂料,通过在配料中加入纳米粒子材料,并选用含氟溶剂和有机硅类消泡剂,保证后期的涂层能够在面料表面形成一层性能稳固的高密度防水层。为了解决上述技术问题,本专利技术所采用的技术方案是:一种纺织用防水涂料,按照重量分数计包括如下组分:聚氨酯树脂30份-45份、偶联剂5份-8份、交联剂6份-12份、纳米粒子材料5份-15份、溶剂12份-15份、颜料0.4份-1.2份、消泡剂1份-3份、增塑剂5份-10份、稳定剂2份-4份;其中溶剂为含氟溶剂,所述消泡剂为有机硅类消泡剂。前述的一种纺织用防水涂料,其特征在于:所述交联剂为过氧化二异丙苯、过氧化苯甲酰中的一种或两种的混合物。前述的一种纺织用防水涂料,其特征在于:所述增塑剂为多元醇酯、氯化烃、柠檬酸酯中的一种或多种的混合物。前述的一种纺织用防水涂料,其特征在于:按照重量分数计包括如下组分:聚氨酯树脂35份、偶联剂6份、交联剂8份、纳米粒子材料12份、溶剂13份、颜料0.8份、消泡剂2份、增塑剂12份、稳定剂3份。前述的一种纺织用防水涂料,其特征在于:按照重量分数计包括如下组分:聚 ...
【技术保护点】
一种纺织用防水涂料,其特征在于:按照重量分数计包括如下组分:聚氨酯树脂30份‑45份、偶联剂5份‑8份、交联剂6份‑12 份、纳米粒子材料5份‑15份、溶剂12份‑15份、颜料 0.4份‑1.2份、消泡剂1份‑3份、增塑剂5份‑10份、稳定剂2份‑4份;其中溶剂为含氟溶剂,所述消泡剂为有机硅类消泡剂。
【技术特征摘要】
1.一种纺织用防水涂料,其特征在于:按照重量分数计包括如下组分:聚氨酯树脂30份-45份、偶联剂5份-8份、交联剂6份-12份、纳米粒子材料5份-15份、溶剂12份-15份、颜料0.4份-1.2份、消泡剂1份-3份、增塑剂5份-10份、稳定剂2份-4份;其中溶剂为含氟溶剂,所述消泡剂为有机硅类消泡剂。2.根据权利要求1所述的一种纺织用防水涂料,其特征在于:所述交联剂为过氧化二异丙苯、过氧化苯甲酰中的一种或两种的混合物。3.根据权利要求1所述的一种纺织用防水涂料,其特征在于:所述增塑剂为多元醇酯、氯化烃、柠檬酸酯中...
【专利技术属性】
技术研发人员:曹永忠,钱学军,
申请(专利权)人:张家港市双河染织有限公司,
类型:发明
国别省市:江苏,32