The invention discloses a resin powder coating formulation, the powder coating formulation for cyclohexane two methanol 300 trihydroxymethylenepropane three 400g, 20 43g 900 1080g, terephthalic acid, acid catalyst 1 5g, 390 490g Rong glycol, excellent performance of the coating surface can be obtained by baking, and has the impact of excellent corrosion resistance, good flexibility and moisture resistance and high impact strength, but also has high weatherability and contamination resistance, powder coating a coating of up to 50 300 mu m, and leveling, not as solvent coating thick coating will drop down or stagnation phenomenon occurred.
【技术实现步骤摘要】
一种树脂粉末涂料配方
本专利技术涉及到一种聚酯树脂粉末涂料的配方。
技术介绍
粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。目前，热固型粉末涂料是以热固性树脂作为成膜物质，加入起交联反应的固化剂经加热后能形成不溶不熔的质地坚硬涂层，温度再高该涂层也不会像热塑性涂层那样软化，而只能发生分解，为于热固性粉末涂料所采用的树脂为聚合度较低的预聚物，分子量较低，所以涂层的流平性较好，具有较好的装饰性，而且低分子量的预聚物经固化后，能形成网状交联的大分子，因而涂层具有较好防腐性和机械性能，故热固性粉末涂料发展尤为迅速，但是，现有技术中，其粉末涂料为聚酯树脂、封闭型异佛尔铜二异氰酸酯、安息香和二丁基锡二月桂酸酯组成，其缺点为物理学性能差、覆盖效果较差，易产生细泡，无法满足电器喷涂和表层保护。
技术实现思路
本专利技术要解决的技术问题是克服上述不足，提供一种具有优良流动性和耐腐蚀性且高冲击强度的粉末涂料的配方。为了解决上述技术问题，通过以下技术方案得以实施：一种树脂粉末涂料配方，所述粉末涂料配...
【技术保护点】
一种树脂粉末涂料配方，其特征在于，所述粉末涂料配方为环乙烷二甲醇300‑400g，三羟甲基丙烷20‑43g，对苯二甲酸900‑1080g，酸催化剂1‑5g，戎二醇390‑490g。
【技术特征摘要】
1.一种树脂粉末涂料配方，其特征在于，所述粉末涂料配方为环乙烷二甲醇300-400g，三羟甲基丙烷20-43g，对苯二甲酸900-1080g，酸催化剂1-5g，戎二醇390-490g。2.根据权...