The invention discloses a Ding Jing rubber aging modified material and preparation method thereof, comprising the following raw materials prepared by weight: 65 75 Ding Jing 20 30 copies of the rubber, polyvinyl acetate, 15 20 nanometer calcium carbonate, 5 10 copies of the modifier, 0.3 0.8 copies of the coupling agent, crosslinking agent, 0.3 0.5 copies of 3 copies of the 1 UV absorbers, 1 3 copies of the invention will be for antioxidant; nano calcium carbonate and Ding Jing rubber modification of the composite, and the nano calcium carbonate is uniformly dispersed in the Ding Jing rubber system, get Ding Jing rubber modified material aging resistance, is conducive to the application in more fields in the Ding Jing rubber.
【技术实现步骤摘要】
一种丁腈橡胶耐老化改性材料及其制备方法
本专利技术涉及改性丁腈橡胶材料领域，具体涉及一种丁腈橡胶耐老化改性材料及其制备方法。
技术介绍
丁腈橡胶是由丁二烯和丙烯腈采用低温乳液聚合法生产制得的，耐油性极好，耐磨性较高，耐热性较好，粘接力强、良好的耐水性、气密性及优良。其缺点是耐低温性差、耐臭氧性差，绝缘性能低劣，弹性稍低。丁腈橡胶广泛用于制各种耐油橡胶制品、多种耐油垫圈、垫片、套管、软包装、软胶管、印染胶辊、电缆胶材料等，在汽车、航空、石油、复印等行业中成为必不可少的弹性材料。随着人们对材料耐老化性能要求的不断提高，未经耐老化改性的丁腈橡胶已难以满足需求，因而，对丁腈橡胶进行耐老化改性成为必要。现今对ABS的耐老化改性处理方法种类繁多，改性效果也很好，尤其是随着纳米材料的出现和应用，丁腈橡胶的耐老化性增加效果显著，使丁腈橡胶能在更多领域大量使用，但也存在不足。纳米材料虽然具有耐老化增强效果好，添加量小的优点，但也存在分散困难，成本高等缺陷。在进行耐老化改性过程中，纳米材料分散不均会影响其耐老化效果，得到的改性材料耐老化性偏低，对改性材料的生产和应用造成不利影响。专利...
【技术保护点】
一种丁腈橡胶耐老化改性材料，其特征在于，包括以下重量份原材料制备得到：65‑75份的丁腈橡胶、15‑20份的纳米碳酸钙、20‑30份的聚醋酸乙烯、5‑10份的改性剂、0.3‑0.8份的偶联剂、0.3‑0.5份的交联剂、1‑3份的紫外线吸收剂、1‑3份的抗氧剂；所述改性剂为三乙醇胺与亚磷酸三苯酯组成的混合物；所述偶联剂为二硬脂酰氧异丙氧基铝酸酯偶联剂，所述交联剂为乙烯亚胺；所述聚醋酸乙烯的聚合度为280‑380；所述丁腈橡胶聚合度为600‑1200。
【技术特征摘要】
1.一种丁腈橡胶耐老化改性材料，其特征在于，包括以下重量份原材料制备得到：65-75份的丁腈橡胶、15-20份的纳米碳酸钙、20-30份的聚醋酸乙烯、5-10份的改性剂、0.3-0.8份的偶联剂、0.3-0.5份的交联剂、1-3份的紫外线吸收剂、1-3份的抗氧剂；所述改性剂为三乙醇胺与亚磷酸三苯酯组成的混合物；所述偶联剂为二硬脂酰氧异丙氧基铝酸酯偶联剂，所述交联剂为乙烯亚胺；所述聚醋酸乙烯的聚合度为280-380；所述丁腈橡胶聚合度为600-1200。2.根据权利要求1所述的改性材料，其特征在于，所述改性剂中三乙醇胺与亚磷酸三苯酯的物质的量之比为1︰1。3.根据权利要求1所述的改性材料，其特征在于，所述聚醋酸乙烯的聚合度为300-350。4.根据权利要求3所述的改性材料，其特征在于，所述聚醋酸乙烯的聚合度为320。5.根据权利要求1所述的改性材料...
【专利技术属性】
技术研发人员：舒春柳，
申请(专利权)人：四川力智久创知识产权运营有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。