The invention discloses a toughened nitrile rubber material and preparation method thereof, which comprises the following parts by weight of raw material preparation: 10 nano glass fiber, 20 copies of 10 copies of the 5 modifier, 15 20 copies, 15 copies of 10 ethylene propylene rubber polystyrene, 60 70 nitrile rubber, 1 coupling agent, 3 copies of 0.5 copies of the 0.3 crosslinking agent; the invention will pass for nano glass fiber and nitrile rubber for modification of the composite, and the nano glass fiber is uniformly dispersed in the nitrile rubber system, tensile strength properties of nitrile rubber material and the same, is conducive to the application nitrile rubber in more areas of.
【技术实现步骤摘要】
一种增韧丁腈橡胶材料及其制备方法
本专利技术涉及改性材料领域，具体涉及一种增韧丁腈橡胶材料及其制备方法。
技术介绍
丁腈橡胶是以甲基丙烯酸甲酯为单体聚合而成的聚合物，是一种热塑性塑料。由于具有耐老化性好、透光性好、绝缘性好、机械强度高、耐候性好、阻燃性好等优异的综合性能，所以长期在电子、电器、机械、汽车、医疗器具、食品加工等领域得到广泛的应用。随着人们对材料拉伸性能要求的不断提高，未经拉伸增强改性的丁腈橡胶已难以满足需求，因而，对丁腈橡胶进行拉伸增强改性成为必要。现今对丁腈橡胶的拉伸增强改性处理方法种类繁多，改性效果也很好，尤其是随着纳米材料的出现和应用，丁腈橡胶的拉伸强度增加效果显著，使丁腈橡胶能在更多领域大量使用，但也存在不足。纳米材料虽然具有拉伸强度增强效果好，添加量小的优点，但也存在分散困难，成本高等缺陷。在进行拉伸强度改性过程中，纳米材料分散不均会影响其拉伸增强效果，得到的改性材料拉伸强度偏低，对改性材料的生产和应用造成不利影响。
技术实现思路
本专利技术的目的在于克服现有丁腈橡胶材料拉伸强度较差的缺陷，提供一种增韧丁腈橡胶材料及其制备方法；本专利技术将经过...
【技术保护点】
一种增韧丁腈橡胶材料，其特征在于，包括以下重量份原材料制备得到：10‑20份的纳米玻璃纤维、5‑10份的改性剂、15‑20份的乙丙橡胶、10‑15份的聚苯乙烯、60‑70份的丁腈橡胶、1‑3份的偶联剂、0.3‑0.5份的交联剂；所述改性剂为苯基磷二酰胺与乙酰柠檬酸三丁酯组成的混合物；所述偶联剂为巯丙基甲基二甲氧基硅烷，所述交联剂为乙烯亚胺；所述聚苯乙烯的聚合度为220‑340；所述丁腈橡胶聚合度为1000‑1600。
【技术特征摘要】
1.一种增韧丁腈橡胶材料，其特征在于，包括以下重量份原材料制备得到：10-20份的纳米玻璃纤维、5-10份的改性剂、15-20份的乙丙橡胶、10-15份的聚苯乙烯、60-70份的丁腈橡胶、1-3份的偶联剂、0.3-0.5份的交联剂；所述改性剂为苯基磷二酰胺与乙酰柠檬酸三丁酯组成的混合物；所述偶联剂为巯丙基甲基二甲氧基硅烷，所述交联剂为乙烯亚胺；所述聚苯乙烯的聚合度为220-340；所述丁腈橡胶聚合度为1000-1600。2.根据权利要求1所述的丁腈橡胶材料，其特征在于，所述改性剂中苯基磷二酰胺与乙酰柠檬酸三丁酯的物质的量之比为1︰1。3.根据权利要求1所述的丁腈橡胶材料，其特征在于，所述聚苯乙烯的聚合度为260-300。4.根据权利要求3所述的丁腈橡胶材料，其特征在于，所述聚苯乙烯的聚合度为280。5.根据权利要求1所述的丁腈橡胶材料，其特征...