The invention discloses an antibacterial titanium aluminum stainless steel composite plate preparation method of panel of gas stove, which comprises the following steps: 1) titanium plate, aluminum foil and stainless steel plate / assembly, the formation of titanium aluminum stainless steel sandwich structure; 2) into the vacuum hot pressing equipment in a few hours, and then processing the pressure and temperature conditions, after cooling, get aluminum stainless steel titanium clad plate. The invention has the advantages of simple operation method, convenient implementation, titanium / aluminum, aluminum / stainless steel interface by uniform diffusion, the metallurgical combination is formed, get stainless steel composite plate titanium aluminum.
【技术实现步骤摘要】
一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法
本专利技术属于铸造
,具体涉及一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法。
技术介绍
随着经济的发展,人们的消费水平、生活质量在不断地提高,人们对公共卫生与个人安全观念也随之发生深刻的变化。抗菌材料的需求与要求也越来越高,抗菌不锈钢的出现迎合了人们对抗菌材料的新要求。
技术实现思路
为了克服现有
存在的上述技术问题,本专利技术的目的在于,提供一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法,通过加入Cu和Ce,采用固溶强化和弥散强化工艺,制备具有抗菌相ε-Cu和Ce元素的奥氏体不锈钢,实现不锈钢的广谱抗菌性能,同时改善不锈钢的抗腐蚀性、耐磨性、强度、韧性、抗氧化性等综合物理化学性能,生产工艺简单,在工业中有较大利用价值,适合工业生产。本专利技术提供的一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法,包括以下步骤:1)将平面尺寸大小一致的钛板、铝箔和不锈钢板进行预处理;2)按照钛-铝-不锈钢的顺序组装;3)将组装好的钛-铝-不锈钢组件,放入热压装置中,预加压后(使材料不易发生移动),以10-30℃/min的加热速度,加热到600-750℃;4)加压至3-5MPa,保温处理1-5小时;5)采用阶梯式冷却方式冷却至室温,取出样品得到钛-铝-不锈钢复合板。本专利技术提供的一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法,其有益效果在于,本专利技术所述方法操作简单,实施方便,可确保钛-铝-不锈钢复合过程中,钛-铝界面,铝-不锈钢界面上,结合均匀,扩散良好;中间铝板的存在,有效的防止了 ...
【技术保护点】
一种用于燃气灶面板的抗菌钛‑铝‑不锈钢复合板制备方法,其特征在于:包括以下步骤:1)将平面尺寸大小一致的钛板、铝箔和不锈钢板进行预处理;2)按照钛‑铝‑不锈钢的顺序组装;3)将组装好的钛‑铝‑不锈钢组件,放入热压装置中,预加压后,以10‑30℃/min的加热速度,加热到600‑750℃;4)加压至3‑5MPa,保温处理1‑5小时;5)采用阶梯式冷却方式冷却至室温,取出样品得到钛‑铝‑不锈钢复合板。
【技术特征摘要】
1.一种用于燃气灶面板的抗菌钛-铝-不锈钢复合板制备方法,其特征在于:包括以下步骤:1)将平面尺寸大小一致的钛板、铝箔和不锈钢板进行预处理;2)按照钛-铝-不锈钢的顺序组装;3)将组装好的钛-铝-不锈钢...
【专利技术属性】
技术研发人员:李玉敏,
申请(专利权)人:青岛天地铸造有限公司,
类型:发明
国别省市:山东,37