一种焊接用还原钛铁矿的制备方法技术

本发明专利技术属于焊接材料制备领域，具体涉及一种焊接用还原钛铁矿的制备方法。本发明专利技术所要解决的技术问题是提供一焊接用还原钛铁矿的制备方法，包括以下步骤：将钛铁矿在流态化反应器中于800～900℃进行氧化，又于1050～1150℃进行还原，然后将物料冷却至室温即可得到还原钛铁矿。本发明专利技术方法制备得到的钛铁矿性能优良，能够改善焊接材料焊接性能。

A preparation method of reductive ilmenite for welding

The invention belongs to the field of welding material preparation, and in particular relates to a preparation method of reducing ilmenite for welding. The technical problem to be solved is to provide a welding method for preparing reduced ilmenite, which comprises the following steps: ilmenite in fluidization reactor at 800~900 DEG C by oxidation and reduction to 1050~1150 DEG C, then the material is cooled to room temperature can be reduced ilmenite. The method prepared by the method has excellent performance of ilmenite and can improve the welding performance of the welding material.

【技术实现步骤摘要】
一种焊接用还原钛铁矿的制备方法
本专利技术属于焊接材料制备领域，具体涉及一种焊接用还原钛铁矿的制备方法。
技术介绍
焊接材料药皮中使用大量的钛系产品，主要起造渣作用，同时可以改善熔渣的流动性，促进焊缝金属还原产物的聚集并把它们排除到熔渣中。增加药皮中TiO2相对含量会使渣壳容易脱落，有效地缩短熔渣凝固温度区间，使熔渣形成所谓的“短渣”，同时还具有一定的稳弧作用。早期的焊条中钛系产品主要以钛白粉和金红石为主，当前焊接材料药皮中加入的钛系产品主要有人造金红石、钛白粉、钛铁矿、还原钛铁矿四种。其中，还原钛铁矿的加入具有还原性好、电弧稳定、熔池平静、增加熔敷效率、电弧柔和、焊缝成型美观、熔渣覆盖好等优良性能。另外，由于其来源稳定，价格适中，已成为普通钛钙型及高钛型焊条药皮的主要原材料。传统还原钛铁矿生产工艺按其生产设备可分为隧道窑工艺、“馒头”窑工艺及回转窑工艺，其原理是将天然钛铁矿与还原剂、脱硫剂按一定比例分层置于专用陶罐内，通过外加热使罐内物料升温至1150℃左右发生氧化还原及脱硫等系列反应，将钛铁矿中的Fe2O3及FeO转化成Fe，冷却后经破碎、筛分及磁选分离即为还原钛铁矿。但是传统还本文档来自技高网...

【技术保护点】
焊接用还原钛铁矿的制备方法，其特征在于：包括以下步骤：将钛铁矿在800～900℃进行氧化反应，然后再在1050～1150℃进行还原反应2～3h，然后冷却至室温即可。

【技术特征摘要】
1.焊接用还原钛铁矿的制备方法，其特征在于：包括以下步骤：将钛铁矿在800～900℃进行氧化反应，然后再在1050～1150℃进行还原反应2～3h，然后冷却至室温即可。2.根据权利要求1所述的焊接用还原钛铁矿的制备方法，其特征在于：所述钛铁矿为攀枝花地区钛铁矿。3.根据权利要求1所述的焊接用还原钛铁矿的制备方法，其特征在于：所述钛铁矿粒...

【专利技术属性】
技术研发人员：刘娟，叶恩东，韩可喜，李凯茂，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51