The invention discloses a production method, in particular discloses a production method of mixed roasting and chrome extraction with chromium containing materials, which belongs to the metallurgical production technology field. A method of producing chromium containing chromium materials by mixed roasting of chromium containing materials is provided with a short process, no sintering, easy implementation and good extraction effect. The production process of soda ash and clinker by chrome, according to 100:50 120:200 400 mass ratio of mixing, crushing, grinding, roasting water leaching process of sodium chromate solution extraction of chromium, the roasting clinker after grinding particle size less than 0.2 mm.
【技术实现步骤摘要】
用含铬物料混合焙烧提铬的生产方法
本专利技术涉及一种生产方法，尤其是涉及一种用含铬物料混合焙烧提铬的生产方法，属于冶金生产工艺
技术介绍
铬矿焙烧提铬按添加填料的种类可分为有钙焙烧法和无钙焙烧法。其中有钙焙烧法需加入2～4倍含钙或镁的填料，虽然解决了铬矿焙烧粘结的技术难题，实现工业化生产，但所得含铬(Cr6+)废渣量大，处理困难，存在很大的环保隐患，目前已逐步被淘汰；近年来积极推广的无钙焙烧法主要是配加提铬尾渣焙烧，一方面是实现了焙烧连续稳定生产，二是含铬废渣量明显减少，环保效益明显，但仍存在尾渣内循环流程长、能耗高、设备利用率低的问题。公开号为CN102557137B的专利公开了一种三段法无钙焙烧生产铬酸钠的方法，以解决现有无钙焙烧生产铬盐存在焙烧效率低、能耗损失大的问题，但因工艺流程冗长，目前还未见大规模化工业生产。
技术实现思路
本专利技术所要解决的技术问题是：提供一种流程简短、焙烧不烧结、易实施，提取效果好的用含铬物料混合焙烧提铬的生产方法。为解决上述技术问题所采用的技术方案是：一种用含铬物料混合焙烧提铬的生产方法，所述的生产方法通过将铬矿、纯碱以及...
【技术保护点】
一种用含铬物料混合焙烧提铬的生产方法，其特征在于：所述的生产方法通过将铬矿、纯碱以及熟料按100:50‑120:200‑400的质量比混均、焙烧、破碎、研磨后水浸获得铬酸钠溶液的工序提取铬，其中，研磨后的焙烧熟料的粒径不超过0.2㎜。
【技术特征摘要】
1.一种用含铬物料混合焙烧提铬的生产方法，其特征在于：所述的生产方法通过将铬矿、纯碱以及熟料按100:50-120:200-400的质量比混均、焙烧、破碎、研磨后水浸获得铬酸钠溶液的工序提取铬，其中，研磨后的焙烧熟料的粒径不超过0.2㎜。2.根据权利要求1所述的用含铬物料混合焙烧提铬的生产方法，其特征在于：所述铬矿的粒径小于0.076㎜，其中Cr2O3的含量为20％-55％。3.根据权利要求2所述的用含铬物料混合焙烧提铬的生产方法，其特征在于：粒径小于0.076㎜的所述铬矿中的Cr2O3的含量为45％-55％。4.根据权利要求1所述的用含...
【专利技术属性】
技术研发人员：何文艺，彭毅，叶露，申彪，陈燕，李明，
申请(专利权)人：攀钢集团攀枝花钢铁研究院有限公司，
类型：发明
国别省市：四川,51