The invention relates to the field of powder metallurgy, in particular to a method for obtaining CuAlO2 powder by the gel combustion method. A preparation method of CuAlO2 powder includes the following steps: Step 1: raw material preparation; step 2: solvent; step 3: forming sol; step 4: preparation of xerogel; step 5: heating; step 6: sintering. The present invention provides a gel combustion method, using nitrate salt instead of alcohol to reduce costs, with citric acid as complexing agent and accelerant, solvent method for preparing CuAlO2 powder with deionized water, ethanol, ethylene glycol, the invention is simple and easy to operate, through the prepared product stable mechanism and performance excellent.
【技术实现步骤摘要】
一种CuAlO2粉末的制备方法
本专利技术涉及粉末冶金
，具体涉及一种凝胶燃烧法制得CuAlO2粉末的方法。
技术介绍
CuAl0，是P型透明导电氧化物材料，直接和间接带隙分别为3．5eV和1.8eV，具有铜铁矿结构。自1997年Kawazoe等⋯提出价带化学修饰理论，并首次用PLD法制备出CuAl02薄膜。迄今为止，许多研究者运用不同的方法制备出了CuAl02薄膜和粉体，如固相反应合成法、离子交换法、水热法、脉冲激光沉积技术、磁控溅射法、化学气相沉积法和溶胶凝胶法等。固相法合成温度高且难以得到超细粉，水热法工艺难以控制。采用溶胶凝胶法制备的CuAl02粉末合成温度较高，粉末团聚严重，且采用的金属醇盐合成过程复杂，后处理繁琐且价格昂贵。
技术实现思路
本专利技术旨在提出一种凝胶燃烧法制得CuAlO2粉末的方法。本专利技术的技术方案在于：一种CuAlO2粉末的制备方法，包括以下步骤：步骤1：原材料准备：铜源：三水硝酸铜；铝源：九水硝酸铝；步骤2：溶剂：分别以去离子水、乙二醇、无水乙醇为溶剂，将三水硝酸铜和九水硝酸铝添加到溶剂中；步骤3：形成溶胶：将上述混合液放置磁...
【技术保护点】
一种CuAlO2粉末的制备方法，其特征在于：包括以下步骤：步骤1：原材料准备：铜源：三水硝酸铜；铝源：九水硝酸铝；步骤2：溶剂：分别以去离子水、乙二醇、无水乙醇为溶剂，将三水硝酸铜和九水硝酸铝添加到溶剂中；步骤3：形成溶胶：将上述混合液放置磁力搅拌器搅拌，搅拌过程中加入柠檬酸，搅拌至溶胶清澈均匀；步骤4：制备干凝胶：将溶胶陈化，在干燥箱中恒温干燥脱水得干凝胶；步骤5：加热：将电热套加热燃烧(约250℃)，将所得黑色疏松粉末研磨均匀；步骤6：烧结：在马弗炉内1100℃煅烧4h。
【技术特征摘要】
1.一种CuAlO2粉末的制备方法，其特征在于：包括以下步骤：步骤1：原材料准备：铜源：三水硝酸铜；铝源：九水硝酸铝；步骤2：溶剂：分别以去离子水、乙二醇、无水乙醇为溶剂，将三水硝酸铜和九水硝酸铝添加到溶剂中；步骤3：形成溶胶：将上述混合液放置磁力搅拌器搅拌，搅拌过程中加入柠檬酸，搅拌至溶胶清澈均匀；步骤4：制备干凝胶：将溶胶陈化，在干燥箱中恒温干燥脱水得干凝胶；步骤5：加热：将电热套加热燃烧(约250℃)，将所得黑...
【专利技术属性】
技术研发人员：郝青，
申请(专利权)人：陕西玉航电子有限公司，
类型：发明
国别省市：陕西,61