氮、硫掺杂的三维碳纳米网络负载二硫化钼纳米材料及制备制造技术
Nitrogen and sulfur doped three dimensional carbon nano network loaded molybdenum disulfide nanomaterials and preparation
The invention relates to a three dimensional carbon nano network loaded molybdenum disulfide nano material, which is doped with nitrogen and sulfur, and provides a preparation method and application. The material is a molybdenum disulfide load in three-dimensional carbon nano network of nitrogen and sulfur doped, the molybdenum disulfide in 100 300nm, three dimensional carbon thickness of nitrogen and sulfur doped 10nm 1, three-dimensional graphene network within a radius of 10 50 m, the mass percentage of molybdenum disulphide and total carbon content in the material (0.3: 0.8 (0.5): 0.2).
【技术实现步骤摘要】
氮、硫掺杂的三维碳纳米网络负载二硫化钼纳米材料及制备
本专利技术涉及一种氮、硫掺杂的三维碳纳米网络负载二硫化钼(MoS2)纳米材料的制备方法与应用，属于电催化析氢材料领域。
技术介绍
随着环境与能源问题的日益突出，人们急需寻求可再生的能量来源和能量载体。H2是一种含量丰富并且可再生的清洁能源，可以用作能量载体来代替化石燃料。产生H2的方法有甲烷气重整、光催化解水、电催化解水等方法。电催化水分解产生H2是一种最高效、最清洁的大规模生产H2的方法，因此人们广泛的研究高效的电催化剂。目前，效率最高的电催化剂是Pt，但是由于Pt价格昂贵而且储量有限，因此限制了其在工业中的大规模应用。寻找一种便宜而且地球储量充足的电催化剂势在必行。其中，MoS2作为一种高效而且稳定的HER电催化而被广泛的研究。但是MoS2的本身导电性较差，不利于其催化性能发挥。目前主要的解决办法有两个：一是将2H相的MoS2通过正丁基锂的插层反应变成1T相的MoS2；二是将MoS2与碳材料复合，从而提高其导电性和电催化析氢性能。
技术实现思路
本专利技术的目的是提供一种氮、硫掺杂的三维碳纳米网络负载二硫化钼纳...
【技术保护点】
一种氮、硫掺杂的三维碳纳米网络负载二硫化钼纳米材料，其特征在于，该材料为二硫化钼纳米片负载在氮、硫掺杂的三维碳纳米网络上，其中二硫化钼纳米片在100‑300nm，氮、硫掺杂的三维碳厚度为1‑10nm，三维石墨烯网络半径在10‑50μm，该材料中二硫化钼与总碳量的质量百分比为：(0.3‑0.8):(0.5‑0.2)。
【技术特征摘要】
1.一种氮、硫掺杂的三维碳纳米网络负载二硫化钼纳米材料，其特征在于，该材料为二硫化钼纳米片负载在氮、硫掺杂的三维碳纳米网络上，其中二硫化钼纳米片在100-300nm，氮、硫掺杂的三维碳厚度为1-10nm，三维石墨烯网络半径在10-50μm，该材料中二硫化钼与总碳量的质量百分比为：(0.3-0.8):(0.5-0.2)。2.一种权利要求1所述结构的氮、硫掺杂的三维碳纳米网络负载二硫化钼纳米材料的制备方法，包括以下步骤：(1).以蔗糖、葡萄糖、柠檬酸、柠檬酸铵中的一种或几种混合为碳源，以四水合仲钼酸铵为钼源，以硫酸钠(Na2SO4)为模板和硫源，以尿素、三聚氰胺、双氰胺中的一种或几种混合为氮源，以碳源中的碳与钼源中的钼摩尔比为(20～100):1，以钼源中的钼与Na2SO4的质量比为1：(10～100)，以碳源中的碳与氮源中的氮摩尔比为(10～10...
【专利技术属性】
技术研发人员：何春年，刁乐晨，赵乃勤，师春生，刘恩佐，马丽颖，何芳，李家俊，
申请(专利权)人：天津大学，
类型：发明