The present invention relates to a method for preparing high temperature resistant coatings for a machine tool comprises the following steps: (1) preparation of high temperature resistant additives; (2) according to the quality of the number of copies, the 15 acrylic resin 30, benzene methyl silicone resin 11 20 copies, 10 copies of 5 castor oil were mixed, mixed time 1 for 1.5 hours, then add Zn powder 2 14 copies, 20 copies of the 15 phenyl ethyl acrylate, isobutyl ether amino resin 25 40 mixing, the mixing time is 1 2H, mixed after high temperature additive added 15 20 copies, the mixing time is 3H, the mixed end products. The production process is simple, the construction is convenient, the operation is easy, the construction period is short, there is no pollution, and the environment is protected.
【技术实现步骤摘要】
一种机床用耐高温涂料的制备方法
本专利技术特别涉及一种机床用耐高温涂料的制备方法。
技术介绍
在工业生产中，很多机器设备是在高温下运行的，因此高温腐蚀值得重视。在各种高温防腐技术中，耐高温涂料具有独特的优越性，因此耐高温涂料在高温防腐领域中应用非常广泛。目前，耐高温涂料可广泛应用于电器、冶金、石油、航空领域、化工、医药、食品等行业各种耐高温设备（例如：暖风机、大功率灯饰、暖气管道、汽车和摩托车消音器、高温炉、烟囱等）。虽然较油性涂料环保，但由于其成本太高和需要高温固化限制了其推广使用。开发低成本耐高温涂料能使环保的涂料代替油漆应用于上述的各种耐高温设备显得尤为重要。
技术实现思路
本专利技术针对上述问题提出了一种机床用耐高温涂料的制备方法。具体的技术方案如下：一种机床用耐高温涂料的制备方法，其特征在于，步骤如下：（1）制备耐高温添加剂，按质量份数计将十六烷基三甲基溴化胺4-9份、硬脂酸钡3-9份、氢氧化铝2-10份、聚二甲基硅氧烷5-10份、丙酮2-8份搅拌混合，混合时间为1-2h，混合结束后得到混合物A；在将有机膨润土5-10份、滑石粉2-6份、碳纤维6-11份进行...
【技术保护点】
一种机床用耐高温涂料的制备方法，其特征在于，步骤如下：（1）制备耐高温添加剂，按质量份数计将十六烷基三甲基溴化胺4‑9份、硬脂酸钡3‑9份、氢氧化铝2‑10份、聚二甲基硅氧烷5‑10份、丙酮2‑8份搅拌混合，混合时间为1‑2h，混合结束后得到混合物A；在将有机膨润土5‑10份、滑石粉2‑6份、碳纤维6‑11份进行混合，混合时间为20‑40min，混合完成后得到混合物B；将混合物A与混合物B进行混合搅拌，混合时间为1‑2H，混合温度为80度，混合完成后得到耐高温添加剂；（2）按质量份数计，将丙烯酸树脂15‑30份、苯甲基硅树脂11‑20份、蓖麻油5‑10份进行混合，混合时间为...
【技术特征摘要】
1.一种机床用耐高温涂料的制备方法，其特征在于，步骤如下：（1）制备耐高温添加剂，按质量份数计将十六烷基三甲基溴化胺4-9份、硬脂酸钡3-9份、氢氧化铝2-10份、聚二甲基硅氧烷5-10份、丙酮2-8份搅拌混合，混合时间为1-2h，混合结束后得到混合物A；在将有机膨润土5-10份、滑石粉2-6份、碳纤维6-11份进行混合，混合时间为20-40min，混合完成后得到混合物B；将混合物A与混合物B进行混合搅拌，混合时间为1-2H，混合温度为...
【专利技术属性】
技术研发人员：朱嬴华，
申请(专利权)人：镇江中焱数控设备有限公司，
类型：发明
国别省市：江苏,32