钴粉的制造方法技术
The manufacturing method of cobalt powder
The invention provides a manufacturing method of cobalt powder, by controlling the adding amount of seeds in the manufacture of cobalt powder by sulfuric acid solution containing cobalt amine complex is to obtain the high reaction efficiency. Manufacturing method of cobalt powder, which is characterized in that a process has experienced to make cobalt powder: mixing procedure, adding amount of cobalt containing the solution in sulfuric acid solution containing cobalt amine complex in more than 1.5 times and 3 times the amount of cobalt powder as a seed, the seed quantity added into the next add 1.5 to 3 wt% of dispersant, the formation of mixed slurry; and reduction and precipitation process, the mixed slurry into the reaction tank, to mixed slurry is injected into the hydrogen, the mixed cobalt complex ions contained in the slurry reduction on the seed surface of cobalt precipitates.
【技术实现步骤摘要】
【国外来华专利技术】钴粉的制造方法
本专利技术涉及由含有硫酸钴氨络物的溶液制造钴粉时具有高反应效率的钴粉制造方法，能够特别适用于由湿式钴冶炼工艺产生的工序内的中间生成溶液的处理。
技术介绍
作为制造微小的钴粉的方法，已知使熔融的钴分散于气体或水中而得到微细粉的雾化法、专利文献1中所公开的通过使钴挥发、在气相中进行还原而得到钴粉的CVD法等干法。另外，作为采用湿法制造钴粉的方法，有专利文献2中公开的使用还原剂生成的方法、专利文献3中公开的通过在高温下向还原气氛中将钴溶液喷雾从而通过热分解反应得到钴粉的喷雾热分解法等。但是，这些方法由于需要价格高的试剂类、大量的能量，因此不能说是经济的方法。另一方面，如非专利文献1中所示那样的、向硫酸钴氨络物溶液中供给氢气将络合物溶液中的钴离子还原而得到钴粉的方法在工业上价格低，是有用的。但是，该方法中具有得到的钴粉粒子容易粗大化的问题。特别地，要从水溶液中使粒子产生并使其生长的情况下，使用如下方法：使称为晶种的微细的结晶少量共存，向其中供给还原剂，使晶种生长而得到规定的粒径的粉末。在该方法中，由于使用的水溶液中的钴浓度、晶种的种类等，不能获得高反应效率...
【技术保护点】
钴粉的制造方法，其特征在于，依次经历下述工序来制作钴粉：混合工序，其中在含有硫酸钴氨络物的溶液中加入上述溶液中含有的钴量的1.5倍以上且3.0倍以下的量的钴粉末作为晶种，接下来加入所加入的晶种量的1.5重量％～3.0重量％的分散剂，形成混合浆料；和还原、析出工序，其中将上述混合浆料装入反应槽内后，向上述混合浆料内吹入氢气，将上述混合浆料中所含的钴络离子还原，在上述晶种表面形成钴析出物。
【技术特征摘要】
【国外来华专利技术】2015.07.03 JP 2015-1347431.钴粉的制造方法，其特征在于，依次经历下述工序来制作钴粉：混合工序，其中在含有硫酸钴氨络物的溶液中加入上述溶液中含有的钴量的1.5倍以上且3.0倍以下的量的钴粉末作为晶种，接下来加入所加入的晶种量的1.5重量％～3.0重量％的分散剂，形成混合浆料；和还原、析出工序，其中将上述混合浆料装入反应槽内后，向上述混合浆料内吹入氢气，...
【专利技术属性】
技术研发人员：山隈龙马，尾崎佳智，高石和幸，平郡伸一，池田修，工藤阳平，土居安夫，
申请(专利权)人：住友金属矿山株式会社，
类型：发明
国别省市：日本,JP