The invention relates to a method for preparing monolithic talcum powder, which comprises the following steps: (1) the talcum powder and surfactant mixed to obtain a mixture A; (2) the blasting agent is added to the steps of (1) A in the mixture, after blasting are a mixture of B; (3) the B mixture after blasting was stripped by shear shear equipment, obtained monolithic talc; compared with the prior art, the prepared monolithic talcum powder with high efficiency and low cost, can be widely used in packing, has broad application prospect in the market.
【技术实现步骤摘要】
一种制备单片滑石粉的方法
本专利技术涉及无机非金属矿物材料领域，尤其涉及一种制备单片滑石粉的方法。
技术介绍
滑石粉是一种白色、柔软的疏水性矿物质,属于含结晶水的硅酸镁结构。它由三层结构组成:两个含硅层中间夹着氧化镁层或氢氧化镁层。不像其它的硅酸盐层状矿物质(如瓷土),滑石粉晶体的三层结构处于完美的电平衡状态，使其本身带有很少的电量或者不带电。缺少电荷使得滑石粉成为非极性或者说疏水性矿物质,这使其能更好地吸附在其它一些疏水性物质如胶粘物和树脂上,这也是为什么滑石粉被广泛用作树脂和胶粘物控制剂的原因。滑石粉是现今最重要的无机化工产品之一。由于滑石粉具有的化学稳定性好、低硬度、层状结构、亲油疏水的优点使得滑石粉不但能起到一般填料的填充、增量、降低成本的作用，而且能增强这些产品的加工性能、机械强度和热力学性能，所以滑石粉被作为填料广泛地应用于造纸、塑料、油漆、陶瓷、化妆品、医药、橡胶、农产品、肥料等行业中。据资料显示，使用单层层状结构的无机材料做填充增强的复合材料与一般使用非单层层状结构的无机材料做填充增强的复合材料相比，能在不损失冲击强度、韧性和透明性的前提下、可以大...
【技术保护点】
一种制备单片滑石粉的方法，其特征在于，包括以下步骤：(1)将滑石粉与表面活性剂混合均匀，得到混合物A；(2)将爆破剂加入到所述步骤(1)中的混合物A中，爆破后得到混合物B；(3)将爆破后得到的混合物B通过剪切设备进行剪切剥离，得到单片滑石粉。
【技术特征摘要】
1.一种制备单片滑石粉的方法，其特征在于，包括以下步骤：(1)将滑石粉与表面活性剂混合均匀，得到混合物A；(2)将爆破剂加入到所述步骤(1)中的混合物A中，爆破后得到混合物B；(3)将爆破后得到的混合物B通过剪切设备进行剪切剥离，得到单片滑石粉。2.根据权利要求1所述的制备方法，其特征在于,所述的表面活性剂包括烯基磺酸盐、十二烷基三甲基氯化铵中的一种或几种。3.根据权利要求1所述的制备方法，其特征在于,所述步骤(1)中的表面活性剂与所述滑石粉的质量比为1：(5-20)。4...
【专利技术属性】
技术研发人员：钟传新，王君，
申请(专利权)人：桂林浩新科技服务有限公司，
类型：发明
国别省市：广西,45
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。