A fireclay insulating refractory brick 0.6 NG120 and a preparation method thereof, relates to the field of refractory material manufacturing technology, refractory brick by weight of raw materials: 20 obturator perlite 25, expanded perlite 10 silica powder 5 15 copies, 10 copies, 15 copies of clay 10, Gao Lvchao 10 fine powder 15, 15 mullite powder 20, water 15 19. The material of the invention adopts high refractoriness raw materials and raw materials according to a certain proportion through batching, mixing, billet, made of fired clay insulating fire brick NG120 0.6, low production costs for the refractory brick, high compressive strength, low heat conduction coefficient, permanent linear change of bulk density, heating temperature and heat preservation time value in the range of GB/T3994 2013 prescribed value.
【技术实现步骤摘要】
一种粘土质隔热耐火砖NG120-0.6及其制备方法
本专利技术涉及耐火材料制造
，尤其涉及一种粘土质隔热耐火砖NG120-0.6及其制备方法。
技术介绍
粘土质隔热耐火砖的生产工艺，国内普遍采用的方法是半干成型法，由于各生产商所用原料、材料的不同以及高温烧成温度和保温时间的差异，96%生产商的产品，加热永久线变化率指标均不合格（达不到GB/T3994-2013指标标准）。造成此种状况的主要原因是烧成温度未达到隔热砖的加热永久线变化温度或在此温度下的保温时间不足，而成品检测时要在规定的温度下保温12h，如果检测的温度和保温时间高于产品烧成温度和保温时间，就会出现隔热砖的加热永久线变化增大，特别是收缩率增大，从而达不到国标的技术指标的要求。由此要想隔热砖的加热永久线变化率合格，就必须要提高隔热砖的烧成温度以及在该温度下的保温时间，才能在规定的高温烧成温度和保温条件下，不收缩或收缩值小，不变形，最终满足国标加热永久线变化率的指标要求。
技术实现思路
本专利技术为了解决上述的现有技术的缺点，提供一种粘土质隔热耐火砖NG120-0.6及其制备方法，该制备方法生产出的成品砖...
【技术保护点】
一种粘土质隔热耐火砖NG120‑0.6，其特征在于：由以下重量份的原料组成：闭孔珍珠岩20‑25份，膨胀珍珠岩 10‑15份，硅石微粉 5‑10份，陶土 10‑15份，高铝超细粉 10‑15份，莫来石粉 15‑20份，水15‑19份。
【技术特征摘要】
1.一种粘土质隔热耐火砖NG120-0.6，其特征在于：由以下重量份的原料组成：闭孔珍珠岩20-25份，膨胀珍珠岩10-15份，硅石微粉5-10份，陶土10-15份，高铝超细粉10-15份，莫来石粉15-20份，水15-19份。2.根据权利要求1所述的粘土质隔热耐火砖NG120-0.6，其特征在于：所述的闭孔珍珠粉颗粒度小于1.2mm，膨胀珍珠岩颗粒度小于2mm，硅石微粉为600目，陶土为200目...
【专利技术属性】
技术研发人员：吕风雷，吕科利，苗承阳，段阳阳，赵更金，
申请(专利权)人：济源市涟源炉业有限公司，
类型：发明
国别省市：河南,41