一种可激光焊接用的改性塑料及其制备方法技术
A modified plastic for laser welding and its preparation method
The invention provides a laser welding with the modified plastics, the modified plastic is added to a perylene black toner business through the laser to the substrate is prepared, the percentage of perylene black toner quality of the modified plastic is 0.05 ~ 5%, the modified plastics in 800 ~ 1100nm laser through. The invention also provides a preparation method for the modified plastic for laser welding. According to the invention, a modified plastic with high laser transmission, easy dyeing, low migration, good weatherability and long term performance and appearance requirements is provided, which greatly expands the application of laser welding technology in the field of automotive interior and exterior decoration.
【技术实现步骤摘要】
一种可激光焊接用的改性塑料及其制备方法
本专利技术涉及材料领域，更具体地涉及一种可激光焊接用的改性塑料及其制备方法。
技术介绍
激光焊接技术是借助激光束产生的热量使塑料接触面熔化，进而将热塑性片材、薄膜或模塑零部件粘结在一起的技术。最常用的激光焊接形式被称为激光透射焊接。激光透射焊接技术的过程为：首先将两个待焊接塑料零部件夹在一起，然后将一束短波红外区的激光定向到待粘结的部位，激光束通过上层材料，然后被下层材料吸收，激光能量被吸收使得下层材料温度升高，熔化上层以及和下层的塑料，从而完成焊接。其中，上层材料可以是透明的或者是有颜色的，但是必须能够保证有足够的激光通过。然而，目前应用在汽车内外饰上的改性材料通常以黑色的外观为主，传统的黑色改性材料如改性PP(聚丙烯)、改性PC(聚碳酸酯)等，但是由于这些材料均采用碳黑.作为颜料，因此对激光的透过率非常低，导致激光焊接无法在这类材料上应用。近些年，苯胺黑开始被作为一种染料加入到30％玻璃纤维增强尼龙中，虽然这种材料可以实现近红外波段的选择透过性，但是此类染料毒性较强，且不能用于改性PP，迁移性高，不能用于汽车领域这种长期...
【技术保护点】
一种可激光焊接用的改性塑料，其特征在于，所述改性塑料是向激光可透过的基材中加入一种苝系黑色色粉制备而成，所述苝系黑色色粉占所述改性塑料的质量百分数为0.05～5％，所述改性塑料在800～1100nm下激光可透过。
【技术特征摘要】
1.一种可激光焊接用的改性塑料，其特征在于，所述改性塑料是向激光可透过的基材中加入一种苝系黑色色粉制备而成，所述苝系黑色色粉占所述改性塑料的质量百分数为0.05～5％，所述改性塑料在800～1100nm下激光可透过。2.根据权利要求1所述的改性塑料，其特征在于，所述激光可透过的基材包括：改性聚丙烯或改性聚碳酸酯。3.根据权利要求2所述的改性塑料，其特征在于，以重量百分比计，所述改性塑料包括以下组分：48～98％聚丙烯，0～25％增韧剂，0～50％玻璃纤维以及0.05～2％苝系黑色色粉，各组分之和等于100％。4.根据权利要求3所述的改性塑料，其特征在于，所述增韧剂选自：乙烯-丙烯共聚物、乙烯-丁烯共聚物或乙烯-辛烯共聚物中的任意一种。5.根据权利要求2所述的改性塑料，其特征在于，以重量百分比计，所述改性塑料包括以下组分：20～80％聚碳酸酯，15～75％改性树脂，0.1％～5％界面相容剂以及0.05～5％苝系黑色色粉，各组分之和等于100％。6.根据权利要求5所述的改性...
【专利技术属性】
技术研发人员：秦玉洁，王俊，
申请(专利权)人：延锋彼欧汽车外饰系统有限公司，
类型：发明
国别省市：上海,31