The invention discloses a preparation method of titanium based graphene high strength polymeric materials, the process of using ultrasonic dispersion technique of graphene oxide and titanium based mixture prepared by homogeneous solution, and then the two solutions with polyvinyl alcohol, two methyl silicone oil, polyvinyl chloride, hydroxyl peroxide cumene and other polymer vacuum refining reaction then, die, microwave heat treatment, ice water bath cooling, drying, to obtain titanium based graphene high strength polymeric materials. The titanium - cornerstone high strength polymer has high hardness, good compression resistance and good application prospect.
【技术实现步骤摘要】
钛基石墨烯高强度聚合材料的制备方法
本专利技术涉及材料这一
，特别涉及到钛基石墨烯高强度聚合材料的制备方法。
技术介绍
石墨烯是由碳六元环组成的两维(2D)周期蜂窝状点阵结构，它可以翘曲成零维(0D)的富勒烯(fullerene)，卷成一维(1D)的碳纳米管(carbonnano-tube，CNT)或者堆垛成三维(3D)的石墨(graphite)，因此石墨烯是构成其他石墨材料的基本单元。石墨烯的基本结构单元为有机材料中最稳定的苯六元环，是目前最理想的二维纳米材料。理想的石墨烯结构是平面六边形点阵，可以看作是一层被剥离的石墨分子，每个碳原子均为sp2杂化，并贡献剩余一个p轨道上的电子形成大π键，π电子可以自由移动，赋予石墨烯良好的导电性。二维石墨烯结构可以看是形成所有sp2杂化碳质材料的基本组成单元。石墨烯及其相关应用技术是目前全球关注的热点，其具有独特的二维结构、高强度、高导电性能和高导热性能等超强的力学和功能特性，被认为是最理想的复合材料增强相，相关课题的研究也成为复合材料领域的热点方向。近些年来，我国已越来越意识到新材料的重要作用，也因此制定了许多相关政...
【技术保护点】
钛基石墨烯高强度聚合材料的制备方法，其特征在于，包括以下步骤：(1)取氧化石墨烯10‑15份，加入25份去离子水，进行超声分散；(2)取二氧化钛2‑4份、钛粉1‑2份，加入10‑15份无水乙醇，进行超声分散；(3)将步骤(1)的石墨烯溶液和步骤(2)的金属钛混合物溶液按照体积比7:3混合，注入真空反应炉内加压加热反应，持续反应30min后，自然降压至常压后依次加入聚乙烯醇2‑5份、二甲基硅油1‑3份、聚氯乙烯2‑5份、过氧化羟基异丙苯1‑2份，混合均与后再次升温至1050‑1100℃，保温反应60‑90min；(4)将步骤(3)所得高温反应液注入模具压模，模具放入微波加热箱...
【技术特征摘要】
1.钛基石墨烯高强度聚合材料的制备方法，其特征在于，包括以下步骤：(1)取氧化石墨烯10-15份，加入25份去离子水，进行超声分散；(2)取二氧化钛2-4份、钛粉1-2份，加入10-15份无水乙醇，进行超声分散；(3)将步骤(1)的石墨烯溶液和步骤(2)的金属钛混合物溶液按照体积比7:3混合，注入真空反应炉内加压加热反应，持续反应30min后，自然降压至常压后依次加入聚乙烯醇2-5份、二甲基硅油1-3份、聚氯乙烯2-5份、过氧化羟基异丙苯1-2份，混合均与后再次升温至1050-1100℃，保温反应60-90min；(4)将步骤(3)所得高温反应液注入模具压模，模具放入微波加热箱内...
【专利技术属性】
技术研发人员：邵光伟，
申请(专利权)人：佛山慧创正元新材料科技有限公司，
类型：发明
国别省市：广东,44