The invention relates to a lead boron polyethylene composite material and a preparation method thereof. The invention belongs to the field of nuclear radiation protection technology, and specifically relates to a composite shielding material and a preparation method thereof. The invention is to solve the problem that the existing material has large particle size, small dispersion and poor interface bonding with polyethylene matrix, resulting in insufficient thermal, mechanical and shielding performance. The number of Pb - B polyethylene composites consists of 55~70 copies of polyethylene, 30~60 Pb and 0.01 ~ 5 portions of boron. Methods: 1. Ingredients; two, mixture; three, prepressure; four, preheating; five, pressing molding. The invention is applied to nuclear power, nuclear power and space radiation protection.
【技术实现步骤摘要】
一种铅硼聚乙烯复合材料及其制备方法
本专利技术属于核辐射防护
，具体涉及一种复合屏蔽材料及其制备方法。
技术介绍
核能作为环保、高效的能源，已越来越受到人们的关注，它广泛应用于核电、核能、军工、宇航、医疗等领域。众所周知，在发生核反应时，会释放出中子、γ射线等对人体、仪器有伤害的射线，故要想让核反应更安全的为人类服务，必须对其进行屏蔽。所以，随着核能与核技术的广泛应用，核屏蔽材料的研发已成为必然趋势。随着核能在核动力领域的广泛应用，核反应堆小型化逐渐被提出，故屏蔽材料在满足核屏蔽性能的同时，材料的减重减型也同样重要。铅硼聚乙烯复合屏蔽材料是一种传统的屏蔽材料，其中聚乙烯具有较高的含氢量，氢原子对快中子具有良好的慢化作用，硼原子能吸收热中子，铅原子除了对具有一定能量的快中子有屏蔽作用外，对γ射线的屏蔽也特别有效。相比其他核屏蔽，铅硼聚乙烯除了具有高效的核屏蔽性能外，还具有质量轻、体积小的特点。它的推广有助于屏蔽结构的简化，能减轻屏蔽材料的重量，缩小材料的体积，能满足材料的减重减型要求，能广泛应用于核电、核动力、空间辐射防护等领域中。然而传统铅硼聚乙烯复合材料中...
【技术保护点】
一种铅硼聚乙烯复合材料，其特征在于铅硼聚乙烯复合材料按重量份数由55～70份聚乙烯、30～60份铅和0.01～5份硼组成。
【技术特征摘要】
1.一种铅硼聚乙烯复合材料，其特征在于铅硼聚乙烯复合材料按重量份数由55～70份聚乙烯、30～60份铅和0.01～5份硼组成。2.根据权利要求1所述的一种铅硼聚乙烯复合材料，其特征在于所述聚乙烯为高密度聚乙烯、高分子量聚乙烯和超高分子量聚乙烯中的一种或其中几种的混合。3.根据权利要求1所述的一种铅硼聚乙烯复合材料，其特征在于所述铅为单质铅粉，粒径为50nm～1μm。4.根据权利要求1所述的一种铅硼聚乙烯复合材料，其特征在于所述硼为单质硼粉，粒径为50nm～1μm。5.根据权利要求1所述的一种铅硼聚乙烯复合材料，其特征在于所述铅硼聚乙烯复合材料按重量份数由55～70份聚乙烯、50～60份铅和0.01～5份硼组成。6.如权利要求1所述的一种铅硼聚乙烯复合材料的制备方法，其特征在于铅硼聚乙烯复合材料的制备方法具体是按以下步骤完成的：一、配料：按重量份数称取55～70份聚乙烯、30～60份铅和0.01～5份硼；二、混料：将步骤一称取的55～70份聚乙烯、30～60份铅和0.01～5份硼进行机械混粉，得到混合粉料；三、预压：将步骤二得到的混合粉料装入模具...
【专利技术属性】
技术研发人员：乔菁，武高辉，何潘婷，王智君，
申请(专利权)人：哈尔滨工业大学，
类型：发明
国别省市：黑龙江,23