A method of catalytic graphitization and a preparation method of super flexible and high thermal conductivity graphene film
The invention discloses a method for catalytic graphitization and the preparation of high thermal conductivity graphene film by using this method. The graphene film is obtained from super large scale homogeneous graphene oxide through solution film formation, chemical reduction and high-temperature pressure reduction. The graphene lamella structure is perfect, the lamellar crystal area is very large (about 100um), and contains few defects. The thickness of interlayer crystallization is large, the structure is dense, and has super high conductivity and thermal conductivity. The graphene film conductivity of 8000 10600S/cm, thermal conductivity of 1800 2600W/mK, can be used as a thermal conductivity apparatus.
【技术实现步骤摘要】
一种催化石墨化的方法以及一种超柔性高导热石墨烯膜的制备方法
本专利技术涉及新型导热材料及其制备方法，尤其涉及一种催化石墨化的方法以及一种超柔性高导热石墨烯膜的制备方法。
技术介绍
2010年，英国曼彻斯特大学的两位教授AndreGeiM和KonstantinNovoselov因为首次成功分离出稳定的石墨烯获得诺贝尔物理学奖，掀起了全世界对石墨烯研究的热潮。石墨烯有优异的电学性能(室温下电子迁移率可达2×105cM2/Vs)，突出的导热性能(5000W/(MK)，超常的比表面积(2630M2/g)，其杨氏模量(1100GPa)和断裂强度(125GPa)。石墨烯优异的导电导热性能完全超过金属，同时石墨烯具有耐高温耐腐蚀的优点，而其良好的机械性能和较低的密度更让其具备了在电热材料领域取代金属的潜力。宏观组装氧化石墨烯或者石墨烯纳米片的石墨烯膜是纳米级石墨烯的主要应用形式，常用的制备方法是抽滤法、刮膜法、旋涂法、喷涂法和浸涂法等。通过进一步的高温处理，能够修补石墨烯的缺陷，能够有效的提高石墨烯膜的导电性和热导性，可以广泛应用于智能手机、智能随身硬件、平板电脑、笔记本电脑等...
【技术保护点】
一种催化石墨化的方法，其特征在于，该方法通过分散于石墨烯片层中的催化剂实现，负载有催化剂的石墨烯高温高压下发生石墨化，所述催化剂选自可溶性铝盐，硅盐，硼化物，镍盐，镁盐，钙盐等，石墨化的条件为1600‑2000℃，20‑60MPa。
【技术特征摘要】
1.一种催化石墨化的方法，其特征在于，该方法通过分散于石墨烯片层中的催化剂实现，负载有催化剂的石墨烯高温高压下发生石墨化，所述催化剂选自可溶性铝盐，硅盐，硼化物，镍盐，镁盐，钙盐等，石墨化的条件为1600-2000℃，20-60MPa。2.一种高导热石墨烯薄膜的制备方法，其特征在于，包含如下步骤：(1)将平均尺寸大于100μm的氧化石墨烯配制成浓度为6～30mg/mL氧化石墨烯水溶液，在溶液中加入质量分数0.1-5％的催化剂(即催化剂在溶液中的质量分数为0.1-5％)；超声分散后，倒在模具板上烘干成氧化石墨烯膜，然后用还原剂进行还原；...