一种耐低温塑料制造技术

本发明专利技术涉及低温塑料领域，公开了一种耐低温塑料，由以下重量份的原料制成：聚氟乙烯树脂25‑32份、聚丙烯均聚物18‑25份、月桂醇12‑17份、四硼酸钠2‑5份、弹性聚乙烯16‑20份、增塑剂8‑12份、相容剂11‑14份、碳酸钙5‑8份、聚氯乙烯树脂粉22‑27份、云母粉3‑6份。本发明专利技术所提供的一种耐低温塑料，提高了塑料在低温环境下的拉伸强度和断裂伸长率，改进了工程塑料在低温环境下的耐受性；并且原料成本较低。

A kind of low temperature resistant plastic

The invention relates to the field of low temperature plastic, discloses a low temperature resistant plastic, made from the following raw materials in weight portion: 25 polyvinyl fluoride resin 32, polypropylene homopolymer 18 25 copies, 17 copies, 12 lauryl sodium borate four 2 5 copies, 20 copies, 16 elastic polyethylene increased 8 plasticizer 12 copies, 14 copies, 11 compatilizers calcium carbonate 5 8 copies, 22 copies of 27 PVC resin powder, mica powder 3 6. A low temperature resistant plastic provided by the invention improves the tensile strength and elongation at break of plastics under low temperature, improves the tolerance of engineering plastics at low temperature, and has low cost of raw materials.

【技术实现步骤摘要】
一种耐低温塑料
本专利技术涉及低温塑料领域，特别是涉及一种耐低温塑料。
技术介绍
塑料，是指以高分子量的合成树脂为主要组分，加入适当添加剂，如增塑剂、稳定剂、阻燃剂、抗菌剂、着色剂等，经加工成型的塑性(柔韧性)材料，或固化交联形成的刚性材料。随着塑料的用途越来越广泛，塑料用品的种类也越来越多。由于塑料自身所展现的诸如质量轻，优良的化学稳定性和电绝缘性及热的不良导体等性能，使塑料的应用领域和地域越来越宽泛。目前使用的塑料制品的使用温度范围比较窄，不能满足需求。在深冷领域、生物领域、食品领域、医药领域会使用到低温液体用于低温处理或保存物品，例如生产中用到的储存液氨用塑料容器、冻存管、冻存架、低温手套等。
技术实现思路
本专利技术旨在提供一种耐低温塑料，以解决现有技术中的上述问题。本专利技术采用的技术方案为：一种耐低温塑料，由以下重量份的原料制成：聚氟乙烯树脂25-32份、聚丙烯均聚物18-25份、月桂醇12-17份、四硼酸钠2-5份、弹性聚乙烯16-20份、增塑剂8-12份、相容剂11-14份、碳酸钙5-8份、聚氯乙烯树脂粉22-27份、云母粉3-6份。优选的，一种耐低温塑料，由以下重量份的本文档来自技高网...

【技术保护点】
一种耐低温塑料，其特征在于，由以下重量份的原料制成：聚氟乙烯树脂25‑32份、聚丙烯均聚物18‑25份、月桂醇12‑17份、四硼酸钠2‑5份、弹性聚乙烯16‑20份、增塑剂8‑12份、相容剂11‑14份、碳酸钙5‑8份、聚氯乙烯树脂粉22‑27份、云母粉3‑6份。

【技术特征摘要】
1.一种耐低温塑料，其特征在于，由以下重量份的原料制成：聚氟乙烯树脂25-32份、聚丙烯均聚物18-25份、月桂醇12-17份、四硼酸钠2-5份、弹性聚乙烯16-20份、增塑剂8-12份、相容剂11-14份、碳酸钙5-8份、聚氯乙烯树脂粉22-27份...

【专利技术属性】
技术研发人员：雷三中，张锐，雷建华，
申请(专利权)人：四川中活低温设备有限公司，
类型：发明
国别省市：四川,51