一种在铌或铌合金表面制备硅化铌涂层的方法技术

本发明专利技术涉及一种在铌或铌合金表面制备硅化铌涂层的方法，以硅粉为原料，采用等离子体喷涂技术在铌或铌合金基体表面制备硅涂层，然后置于惰性气氛中在1000～1500℃下热处理1～10小时，从而在基体表面形成硅化铌涂层。本发明专利技术所述制备方法具有工艺简单、成本低、效率高、可重复性好、适合规模化生产等优点，具有广阔的应用前景。

A method for the preparation of niobium silicide coating on the surface of niobium or niobium alloy

The invention relates to a method for preparing niobium silicide coating on niobium or niobium alloy surface, with silicon powder as raw material, using the technology of preparation of silicon coating on the surface of niobium or niobium alloy by plasma spraying, and then placed in an inert atmosphere at 1000~1500 DEG C for 1~10 hours of heat treatment, thus niobium silicide coating is formed on the surface of the substrate. The preparation method of the invention has the advantages of simple process, low cost, high efficiency, good repeatability, and suitable for large-scale production, and has wide application prospects.

【技术实现步骤摘要】
一种在铌或铌合金表面制备硅化铌涂层的方法
本专利技术涉及一种硅化物涂层的制备方法，特别涉及一种在铌或铌合金表面制备具梯度结构的硅化铌涂层的方法，属于高温涂层

技术介绍
铌(Nb)是一种高熔点(2468℃)的难熔金属，密度适中，耐腐蚀，抗辐射，同时高温强度大，具有良好的高温机械性能。铌与铌合金的优良特性使其成为航空、航天与核工业中高温结构件的重要候选材料之一，可用来制造火箭发动机、核反应堆等关键部件。然而，其氧化性能较差，纯铌在600℃就发生“pest”氧化现象，且随着温度的升高，氧化程度加剧，最终导致其高温性能的失效，这一缺点严重制约了铌与铌合金的应用。为了改善其高温抗氧化性能，表面涂层保护是兼顾铌与铌合金高温力学性能与抗氧化性能切实有效的途径。二硅化铌(NbSi2)氧化时表面能够形成SiO2氧化膜，该氧化膜致密且具备自愈合能力，具有良好的高温抗氧化能力，从而使得NbSi2成为铌与铌合金高温防护涂层的主要选择。Suzuki等人采用熔盐法在铌基体表面沉积一层NbSi2涂层【1.R.Suzuki,M.Ishikawa,K.Ono,NbSi2coatingonniobiumusi本文档来自技高网...

【技术保护点】
一种在铌或铌合金表面制备硅化铌涂层的方法，其特征在于，以硅粉为原料，采用等离子体喷涂技术在铌或铌合金基体表面制备硅涂层，然后置于惰性气氛中在1000～1500℃下热处理1～10小时，从而在基体表面形成硅化铌涂层。

【技术特征摘要】
1.一种在铌或铌合金表面制备硅化铌涂层的方法，其特征在于，以硅粉为原料，采用等离子体喷涂技术在铌或铌合金基体表面制备硅涂层，然后置于惰性气氛中在1000～1500℃下热处理1～10小时，从而在基体表面形成硅化铌涂层。2.根据权利要求1所述的方法，其特征在于，所述硅粉的粒径为10～120μm，纯度大于98wt.%。3.根据权利要求1或2所述的方法，其特征在于，所述基体经过表面喷砂预处理，所述喷砂预处理的压强为0.1～0.5MPa。4.根据权利要求1-3中任一项所述的方法，其特征在于，所述等离子体喷涂技术的工艺参数包括：等离子体气体Ar：30～50slpm；等离子体气体H2：6～15slpm；粉末载气...

【专利技术属性】
技术研发人员：牛亚然，翟翠红，黄利平，李红，郑学斌，孙晋良，丁传贤，
申请(专利权)人：中国科学院上海硅酸盐研究所，
类型：发明
国别省市：上海,31