一种玻璃纤维板材防水添加剂及其制备工艺制造技术

一种玻璃纤维板材防水添加剂，包括以下重量份材料：石蜡55‑60份、十二烷基苯磺酸钠5‑10份、油酸三乙醇胺10‑12份、平平加15‑18份、乳白灵3‑5份、溶剂20‑35份。本发明专利技术提供了一种玻璃纤维板材防水添加剂及其制备工艺，采用油酸三乙醇胺、平平加和乳白灵这三种乳化剂的复合，由于它们的亲水亲油平衡值、结构、类型均不相同，使得这几种乳化剂的复合达到更好的效果，不仅使得乳化添加剂中的亲水成分全部自然分解，消除了对防水性能的影响，还增加了防水性能的稳定性。

A waterproof additive for glass fiber sheet and its preparation technology

Waterproof additive for fiber glass plate, including the following parts by weight of materials: 55 paraffin 60 copies, 10 copies, 5 twelve sodium 10 triethanolamine oleate 12, Pimpinga 18, Ling Bai 15 milk 3 5 copies, 35 copies of 20 solvent. The present invention provides a glass fiber sheet waterproof additive and its preparation process, using compound triethanolamine oleate, peregal and milk Ling Bai this three kinds of emulsifiers, due to their HLB value, structure and types are not the same, the emulsifier compound to achieve better effect, not only makes the hydrophilic component emulsion all the additives in the natural decomposition, eliminates the influence of waterproof performance, but also increased the stability and waterproof performance.

【技术实现步骤摘要】
一种玻璃纤维板材防水添加剂及其制备工艺
本专利技术属于防水材料领域，具体涉及一种玻璃纤维板材防水添加剂及其制备工艺。
技术介绍
现在国内纤维板行业发展很快，随着对纤维板质量要求越来越高，就越需要所用防水材料具备用量少但抗水性强的特性。由于乳化蜡颗粒度小，在纤维板制造过程中通过有效的破乳使微小的蜡颗粒从水相析出，均匀地吸附在木纤维上，从而达到耗蜡量低、抗水性好的要求。国内的木材行业，虽然也以石蜡作为防水添加剂，但大多数是以固体石蜡或熔化石蜡作为防水添加剂，与胶料配伍不好，产品质量差。极少使用乳化蜡的厂家也用简单的方法自行乳化，产品稳定性差，质量达不到要求，同时也造成了蜡原料的极大浪费。因而，在纤维板行业，非常需要一种适合于现有工艺的乳化蜡防水添加剂产品。专利01135227.2公开了一种矿棉吸声板用乳化石蜡防潮剂及其制法，它的组分中包括石蜡、改性树脂、非离子表面活性剂组合物和助乳化剂，其重量组成如下：石蜡∶改性树脂∶非离子表面活性剂组合物∶助乳化剂∶水＝5-22∶5-20∶0.5-5∶2-8∶余量。此专利技术申请技术方案中加入改性树脂成分，但乳液浓度只有30％，乳化剂中亲水成分也不能自本文档来自技高网...

【技术保护点】
一种玻璃纤维板材防水添加剂，其特征在于，包括以下重量份材料：

【技术特征摘要】
1.一种玻璃纤维板材防水添加剂，其特征在于，包括以下重量份材料：2.一种权利要求1所述的一种玻璃纤维板材防水添加剂的制备工艺，其特征在于，步骤包括：将石蜡、十二烷基苯磺酸钠、油酸三乙醇胺、平平加、乳白灵和溶剂按照比例混合搅拌，控制温度在100-110℃，蜡...