一种铜/石墨导电滑板材料的制备方法技术
A preparation method of copper / graphite conductive slider material
The invention relates to a preparation method of a copper / graphite conductive slide plate material, which belongs to the technical field of contact sliding material for electric locomotive. The invention adopts the technology of ball milling and mixing powder, powder forming and sintering, shaping processing and plastic shaping to prepare copper / graphite conductive slider material. The method can make use of existing production equipment, with less investment and low production cost, and can fully improve the interfacial wettability between graphite and copper substrate, and obtain copper based skateboard material with self lubrication and good conductivity.
【技术实现步骤摘要】
一种铜/石墨导电滑板材料的制备方法
本专利技术涉及一种铜/石墨导电滑板材料的制备方法，属于电力机车接触滑动材料
技术介绍
随着高速铁路的发展，高铁速度已经达到每小时300-350公里，这样高的运行速度对机车部件的性能要求非常高，而滑板是连接机车和电线的重要集电受流装置。在电力机车高速行驶中，滑板和接触线之间发生高速相对的带电摩擦，这就必然要求导电滑块材料不仅要具有良好的导电性、摩擦磨损性，而且又要保证不对导线造成严重的损伤，不降低导线的寿命。铜基粉末冶金滑板是重要的导电滑板材料。传统的粉末冶金滑板是将金属粉和自润滑相粉末充分混合，混合粉末再经过压制成形、烧结、复压复烧、挤压拉拔或轧制工艺获得导电滑板材料。这种制备方法容易造成粉末界面污染、界面结合差，致密度低、导电性差；特别是对于铜石墨滑板材料而言，由于石墨与铜界面润湿性差，导致使用过程中石墨颗粒容易从铜基体脱落，自润滑效果急剧降低，对导线造成损伤严重。
技术实现思路
本专利技术针对现有技术的不足，提供一种铜/石墨导电滑板材料的制备方法，即通过沥青为介质来改善铜基体与石墨的界面润湿性，采用球磨混粉、粉末成形与...
【技术保护点】
一种铜/石墨导电滑板材料的制备方法，其特征在于，具体步骤为：（1）将铜粉和沥青混合均匀并进行球磨处理3~36h得到混合物A；（2）将石墨与锡粉混合均匀并进行球磨处理3~36h得到混合物B；（3）将步骤（1）所得混合物A与步骤（2）所得混合物B混合均匀并进行球磨处理3~36h得到混合物C；（4）在压力为500~900Mpa的条件下，将步骤（3）所得混合物C压制成型得到坯体；（5）将步骤（4）所得坯体进行真空烧结处理，冷却即得锭坯；（6）在压力为800~1200 MPa的条件下，将步骤（5）所得锭坯挤压成滑板条形，整形即得铜/石墨导电滑板材料。
【技术特征摘要】
1.一种铜/石墨导电滑板材料的制备方法，其特征在于，具体步骤为：（1）将铜粉和沥青混合均匀并进行球磨处理3~36h得到混合物A；（2）将石墨与锡粉混合均匀并进行球磨处理3~36h得到混合物B；（3）将步骤（1）所得混合物A与步骤（2）所得混合物B混合均匀并进行球磨处理3~36h得到混合物C；（4）在压力为500~900Mpa的条件下，将步骤（3）所得混合物C压制成型得到坯体；（5）将步骤（4）所得坯体进行真空烧结处理，冷却即得锭坯；（6）在压力为800~1200MPa的条件下，将步骤（5）所得锭坯挤压成滑板条形，整形即得铜/石墨导电滑板材料。2.根据权利要求1所述铜/...
【专利技术属性】
技术研发人员：周晓龙，姚碧霞，曹建春，黎敬涛，
申请(专利权)人：昆明理工大学，
类型：发明
国别省市：云南,53