The invention discloses an elastic cashmere is not inverted, with spandex or lycra and bright polyester filament yarn as warp woven elastic fabric, fabric dyeing and finishing were not cashmere; not cashmere thickness is 1 1.5 mm, one side is provided with a plush; according to the weight percentage of spandex or Leica content is 5 6%, bright polyester filament is 94 95%, the preparation method comprises the fabric weaving and dyeing stereotypes. The four side projectiles of the invention can not fall down, have good vertical character, good durability and comfort, long service life and wide application range.
【技术实现步骤摘要】
一种四面弹不倒绒及其制备方法
:本专利技术涉及纺织领域,具体讲是一种四面弹不倒绒及其制备方法。
技术介绍
:现有的弹力面料编织方法复杂,毛面竖直性、舒适性和耐用性欠佳,限制了弹力面料的运用范围。
技术实现思路
:本专利技术所要解决的技术问题是,提供一种毛面竖直性好,耐用性和舒适性好的四面弹不倒绒,该不倒绒设计独特,操作简单、使用寿命长,运用范围广。本专利技术的技术解决方案是,提供一种四面弹不倒绒,采用氨纶或莱卡与大有光涤纶长丝作为经纱织成弹力坯布,坯布经染整后制得不倒绒;不倒绒厚度为1.0-1.5毫米,其中一面设有毛绒;按重量百分比,氨纶或莱卡含量为5-6%,大有光涤纶长丝为94-95%。本专利技术所要解决的另一技术问题是,提供一种四面弹不倒绒的制备方法,包括下列步骤:a,坯布织造,b,染色定型,其中,坯布织造包括以下步骤,(1)原料采购;(2)纱线整经;(3)织机织造形成坯布;染色定型包括以下步骤,(1)剪毛;(2)烫光;(3)坯布定型;定型机速度为:45±2m/分钟,温度为:185-195±2℃;(4)染色;染色温度为:120±2℃,速度为:90±2m/min;(5)色坯定型;(6)烫光;(7)成品。本专利技术与现有技术相比,具有以下有益效果,本专利技术的四面弹不倒绒设计独特,操作简便,容易实现,其采用具有优异弹性性能的氨纶纤维和有光涤纶长丝原料,以特定的工艺条件编织正面毛绒结构,不仅提高了面料的光亮度和服用性能,同时又赋予其良好的毛面竖直性和舒适性,有助于提高面料的使用寿命,广泛用于服装,沙发等领域市场前景广阔。具体实施方式:下面就具体实施方式对本专利技 ...
【技术保护点】
一种四面弹不倒绒,其特征在于:采用氨纶或莱卡与大有光涤纶长丝作为经纱织成弹力坯布,坯布经染整后制得不倒绒;不倒绒厚度为1.0‑1.5毫米,其中一面设有毛绒;按重量百分比,氨纶或莱卡含量为5‑6%,大有光涤纶长丝为94‑95%。
【技术特征摘要】
1.一种四面弹不倒绒,其特征在于:采用氨纶或莱卡与大有光涤纶长丝作为经纱织成弹力坯布,坯布经染整后制得不倒绒;不倒绒厚度为1.0-1.5毫米,其中一面设有毛绒;按重量百分比,氨纶或莱卡含量为5-6%,大有光涤纶长丝为94-95%。2.一种四面弹不倒绒的制备方法,其特征在于,包括下列步骤:a,坯布织造,b,染色定型...
【专利技术属性】
技术研发人员:徐亚伟,
申请(专利权)人:浙江新千禧纺织股份有限公司,
类型:发明
国别省市:浙江,33