一种高纯铝的提纯方法技术

本发明专利技术涉及一种高纯铝的提纯方法，通过将熔融的铝液注入坩埚中，且通过坩埚加热，使设置在坩埚中部的结晶器在坩埚内螺旋式旋转，对坩埚内的铝液进行搅拌，并不断向结晶器内通入冷却水，进行冷却结晶。本发明专利技术的优点在于：通过坩埚外表面的加热丝使铝液保持在一定的温度，并向结晶器中不断加入冷却水，铝液就会在结晶器周围结晶出纯度高的晶体；这种工艺简单，且生产效率高；同时，提纯后铝的纯度可高达99.9999%。

A purification method for high purity aluminum

The invention relates to a purifying method of high pure aluminum, the aluminum melting liquid into the crucible and the crucible, through heating, the mold is arranged in the middle of the pot in the crucible rotating, aluminum liquid inside the crucible for mixing, and continue to mold into the cooling water for cooling. Crystallization. The invention has the advantages that the heating wire through the crucible outer surface of the molten aluminum is maintained at a certain temperature, and to continue to join in the mould cooling water, liquid aluminum will crystallize high purity crystals in the mold around; the process is simple, and the production efficiency is high; at the same time, the high purity aluminum after purification 99.9999%.

【技术实现步骤摘要】
一种高纯铝的提纯方法
本专利技术涉及金属铝的提纯方式，特别涉及一种高纯铝的提纯方法。
技术介绍
尽管国内有企业已在试生产或规模化生产高纯铝，但与国外同类企业相比，有较大差距，存在多方不足：1.设备及工艺相对复杂，其利用多学科领域技术，使投资成本过大，且不便掌握操控；2.排出杂质效率并不理想，生产不出合格产品；3.能耗偏高，达15000KWH/吨以上，与国家节能减排政策相违，尽管目前有所降低，但也有万度左右；4.尽管生产出产品，但质量尚不稳定，使国内用户无法使用。
技术实现思路
本专利技术要解决的技术问题是提供一种工艺简单且提纯效果好的高纯铝的提纯方法。为解决上述技术问题，本专利技术的技术方案为：一种高纯铝的提纯方法，其创新点在于：包括以下步骤：（1）将熔融的铝液注入坩埚中，且通过坩埚加热，使铝液保温在680℃；（2）使设置在坩埚中部的结晶器在坩埚内螺旋式旋转，对坩埚内的铝液进行搅拌，并不断向结晶器内通入冷却水，进行冷却结晶。本专利技术的优点在于：本专利技术高纯铝的提纯方法，通过坩埚加热使铝液保持在一定的温度，并向结晶器中不断加入冷却水，铝液就会在结晶器周围结晶出纯度高的晶体，并通过不断旋本文档来自技高网...

【技术保护点】
一种高纯铝的提纯方法，其特征在于：包括以下步骤：（1）将熔融的铝液注入坩埚中，且通过坩埚加热，使铝液保温在680℃；（2）使设置在坩埚中部的结晶器在坩埚内螺旋式旋转，对坩埚内的铝液进行搅拌，并不断向结晶器内通入冷却水，进行冷却结晶。

【技术特征摘要】
1.一种高纯铝的提纯方法，其特征在于：包括以下步骤：（1）将熔融的铝液注入坩埚中，且通过坩埚加热，使铝液保温在680℃...

【专利技术属性】
技术研发人员：曹建民，
申请(专利权)人：如皋市下原科技创业服务有限公司，
类型：发明
国别省市：江苏,32