The invention discloses a molding method of the modified biomass fuel in the field of biomass fuel preparation technology. The preparation method of molding fuel including the biomass materials to break for the diameter of 1cm particles; in limited oxygen or anaerobic conditions, rapid heat treatment, heat collecting and receiving modified biomass; the modified biomass thermal crushing treatment, adding binder mixed in the molding machine molding preparation fuel. Can destroy the structure of the fiber raw materials, reduce its flexibility, makes it easier to crushing and grinding, grinding and shaping can significantly reduce the energy consumption, but also significantly improve the calorific value and stability of briquette; in addition to liquid by-products as binder, thereby forming the block process made without heating, thus reducing the wear of mechanical equipment and also can improve the durability of briquette. The cost of preparation is effectively reduced.
【技术实现步骤摘要】
一种改性生物质燃料的成型方法
本专利技术属于生物质燃料制备
，特别涉及一种改性生物质燃料的成型方法。
技术介绍
生物质燃料成型是将秸秆、稻壳、木屑等生物质废弃物，用机械加压的方法，使原来松散、无定形的原料压缩成具有一定形状、密度较大的固体成型燃料。压缩生物质成型燃料具有体积小、密度大、储运方便、热值高、燃烧稳定等优点。然而，生物质独特的纤维结构，导致连续加料困难，粉碎能耗较高；生物质原料密度小、无粘结性，在压制过程中通常伴随着原始颗粒的弹性变形、表面破坏和塑性变形，这个过程要消耗大量的能量；生物质原料种类和含水量变化范围宽，导致成型困难且燃料品质不一，燃料点火和燃烧性能波动较大。这些因素导致生物质成型燃料成本偏高，难以大规模推广。因此，为大规模生产低成本的生物质成型燃料，迫切需要开发低能耗生物质成型燃料生产技术。
技术实现思路
本专利技术的目的是提供一种改性生物质燃料的成型方法，其特征在于，包括下述步骤：1)在热处理前将生物质材料破碎至直径为1cm以下的颗粒；2)将生物质材料在氧当量比小于0.1的有限供氧或者无氧条件下，在300-500℃温度下进行快速热处理0....
【技术保护点】
一种改性生物质燃料的成型方法，其特征在于，包括下述步骤：1)在热处理前将生物质材料破碎至直径为1cm以下的颗粒；2)将生物质材料在氧当量比小于0.1的有限供氧或者无氧条件下，在300‑500℃温度下进行快速热处理0.01‑5s，收集并获得热改性生物质以及少量液体副产物和伴生气；3)以步骤2)得到的热改性生物质为原料，对其进行粉碎处理，以液体副产物为粘结剂，或再另外添加粘结剂组成混合粘结剂，于成型机中制备成型燃料。
【技术特征摘要】
1.一种改性生物质燃料的成型方法，其特征在于，包括下述步骤：1)在热处理前将生物质材料破碎至直径为1cm以下的颗粒；2)将生物质材料在氧当量比小于0.1的有限供氧或者无氧条件下，在300-500℃温度下进行快速...
【专利技术属性】
技术研发人员：张强，
申请(专利权)人：爱诺威尔新能源科技天津有限公司，
类型：发明
国别省市：天津,12