一种湿拌砂浆外加剂制造技术

本发明专利技术涉及一种湿拌砂浆外加剂，所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20‑40份、木质素磺酸钠20‑30份、引气剂0.6‑1.0份和粉煤灰900‑1000份。本发明专利技术的优点在于：本发明专利技术湿拌砂浆外加剂，其中，纤维素醚的加入，起到保水增稠作用；引气剂，可以提高砂浆和易性，增大砂浆的得率；以粉煤灰为填料，可有效阻止砂浆反碱的形成；此外，木质素磺酸钠减水剂的使用，可以减少水的用量提高砂浆早期强度。

A kind of wet mixed mortar admixture

The invention relates to a wet mortar admixture, the wet mortar admixture is composed of the following components in part by weight: 20 cellulose ether 40, sodium ligninsulfonate 20 30 copies, 1 copies of 0.6 air entraining agent and fly ash 900 1000. The invention has the advantages that the invention of wet mix mortar admixture, which adding cellulose ether, hold water thickening effect; air entraining agent, can improve the workability of mortar, mortar increased yield; using fly ash as filler, which can effectively prevent the formation of mortar anti alkali; in addition, lignin sulfonate superplasticizer can reduce the amount of water use, improve the early strength of mortar.

【技术实现步骤摘要】
一种湿拌砂浆外加剂
本专利技术属于建筑材料
，特别涉及一种湿拌砂浆外加剂。
技术介绍
近年来随着人们对环境问题关注度的日益提高，城市建设进程的加快，建设过程中产生的大量粉尘也成了城市环境污染物的主要来源之一。据统计，施工扬尘占城区粉尘排放量的23％，其中现场使用水泥、砂、石的粉尘排放量占施工扬尘总量的36％。传统的建筑砂浆在现场搅拌时，一般都没有封闭的作业现场，严重影响空气质量。特别是2013年以来全国大部分地区出现的雾霾天气，让人们重新对生态环境保护中的扬尘污染加以重视。相对于商品砂浆来说，现场搅拌砂浆也有大量的技术性缺点，比如砂浆施工性差、收缩率大、强度不稳定、抗渗性差等等问题。针对于以上出现的各类问题，各地政府也相继出台了以预拌砂浆取缔现场搅拌砂浆的文件。本专利技术就针对预拌砂浆中的湿拌砂浆而研发了一种湿拌砂浆所使用的外加剂。
技术实现思路
本专利技术要解决的技术问题是提供一种湿拌砂浆外加剂，以解决上述问题。为解决上述技术问题，本专利技术的技术方案为：一种湿拌砂浆外加剂，其创新点在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20-40份、木质素磺酸钠20-30份、本文档来自技高网...

【技术保护点】
一种湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20‑40份、木质素磺酸钠20‑30份、引气剂0.6‑1.0份和粉煤灰900‑1000份。

【技术特征摘要】
1.一种湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组分组成：纤维素醚20-40份、木质素磺酸钠20-30份、引气剂0.6-1.0份和粉煤灰900-1000份。2.根据权利要求1所述的湿拌砂浆外加剂，其特征在于：所述湿拌砂浆外加剂是由以下重量份的组...