The invention discloses a high strength pumping agent and a preparation method, which belongs to the field of building material. The pumping agent according to the percentage of the total weight of raw material, consisting of the following ingredients: beta iodate naphthalene formaldehyde condensates, 35 45% modified naphthalene sulfonic acid formaldehyde condensation product of sodium gluconate, 25% 15 2 4% twelve, sodium dodecyl sulfate, 1 3% hydroxypropyl starch ether 4 6%, C 0.5 0.9% hydroxyl methyl cellulose, polyvinyl alcohol and water 0.9% 0.3 15.8 32.2%. The invention also discloses the preparation method of the pumping agent. The pumping agent of the invention has high strength, stable performance, and has the effect of high fluidization, adhesion, lubrication and retarding. It has a wide range of application and good water reducing.
【技术实现步骤摘要】
一种高强泵送剂及其制备方法
本专利技术涉及一种高强泵送剂及其制备方法，属于建筑材料制造领域。
技术介绍
混凝土是建筑业中重要的建材。泵送剂是指能改善混凝土拌合物泵送性能的外加剂。所谓泵送性能，就是混凝土拌合物具有能顺利通过输送管道、不阻塞、不离析、粘塑性良好的性能。传统的泵送剂，粘聚力低，不适应大规模工业化使用。随着土建施工技术发展，对混凝土的要求越来越高，要求应用C60，C80至C100高强度混凝土的越来越广泛，因此，有必要研究一种高强泵送剂，以解决现有技术的不足。
技术实现思路
本专利技术的目之一，是提供一种高强泵送剂。本专利技术的泵送剂，能提高混凝土的抗渗、抗冻、耐久性，能降低混凝土坍落度损失，减水性良好，无氟低碱，对钢筋无锈蚀作用，不会出现碱骨料反应，适合于长距离的运输及泵送施工，适用范围广。本专利技术解决上述技术问题的技术方案如下：一种高强泵送剂，按原料总重量的百分含量计，由如下各原料组成：β-萘碘酸盐甲醛缩合物35-45％、改性萘磺酸甲醛缩合物15-25％、葡萄糖酸钠2-4％、十二烷基硫酸钠1-3％、羟丙基淀粉醚4-6％、羟丙甲基纤维素0.5-0.9％、聚...
【技术保护点】
一种高强泵送剂，其特征在于，按原料总重量的百分含量计，由如下各原料组成：β‑萘碘酸盐甲醛缩合物35‑45％、改性萘磺酸甲醛缩合物15‑25％、葡萄糖酸钠2‑4％、十二烷基硫酸钠1‑3％、羟丙基淀粉醚4‑6％、羟丙甲基纤维素0.5‑0.9％、聚乙烯醇0.3‑0.9％和水15.8‑32.2％。
【技术特征摘要】
1.一种高强泵送剂，其特征在于，按原料总重量的百分含量计，由如下各原料组成：β-萘碘酸盐甲醛缩合物35-45％、改性萘磺酸甲醛缩合物15-25％、葡萄糖酸钠2-4％、十二烷基硫酸钠1-3％、羟丙基淀粉醚4-6％、羟丙甲基纤维素0.5-0.9％、聚乙烯醇0.3-0.9％和水15.8-32.2％。2.根据权利要求1所述的一种高强泵送剂，其特征在于，原料总重量的百分含量计，由如下各原料组成：β-萘碘酸盐甲醛缩合物40％、改性萘磺酸甲醛缩合物20％、葡萄糖酸钠3％、十二烷基硫酸钠2％、羟丙基淀粉醚5％、羟丙甲基纤维素0.7％、聚乙烯醇0.6％和...
【专利技术属性】
技术研发人员：张朝阳，
申请(专利权)人：贵州凯襄新材料有限公司，
类型：发明
国别省市：贵州,52