一种整体式介孔碳材料及其制备方法技术
A holistic mesoporous carbon material and its preparation method
The present invention provides an integral mesoporous carbon material and a preparation method. The preparation method comprises the following steps: seafood shell heat treatment, then adding the solution of organic amine precursor, reaction at room temperature 1H 300h, obtain a mixed solution; the mixed liquid centrifugal purification after vacuum drying, and then treated by carbonation in 0.5M hydrochloric acid solution in 3M, in under the condition of normal temperature treatment of 1H 10h, obtained monolithic mesoporous carbon materials; wherein, the quality of the seafood shell and organic amine precursor is 30: (4 8). The invention also provides an integral mesoporous carbon material obtained by the preparation method mentioned above.
【技术实现步骤摘要】
一种整体式介孔碳材料及其制备方法
本专利技术属于纳米材料制备的
，涉及一种整体式介孔碳材料及其制备方法。
技术介绍
介孔碳是近年来发现的一类新型多孔材料，指的是尺寸在2-50纳米的碳材料，其比表面可达2500m2·g-1，孔容可达2.25cm3·g-1，同时它具有良好的导电性、化学惰性和耐腐蚀性，且孔径可调，因此，介孔碳在催化、吸附、分离、储氢、电化学等方面有很好的潜在应用价值。介孔碳整体式孔结构是指介孔碳的孔道结构相互平行，孔道尺寸均一。制备介孔碳通常采用的方法包括模板法和CVD方法，相对于模板法，CVD等物理方法可以制备出高质量的介孔碳材料，但成本较高。模板法分为硬模板和软模板法，硬模板一般采用介孔氧化硅(Chem.Commun.1999,1955)，软模板法一般采用有机大分子如表面活性剂和前驱物相互作用形成介孔结构。碳源前驱物通常采用葡萄糖、蔗糖乙炔、中间相沥青、呋喃甲醇、苯酚/甲醛树脂等。通过浸渍或气相沉积等方法，碳源前驱物进入介孔氧化硅的孔道中，在酸催化作用下热分解碳化该碳源前驱物，碳因此沉积在模板的孔道内，最后用NaOH或HF溶解掉SiO2模板，...
【技术保护点】
一种整体式介孔碳材料的制备方法，其包括以下步骤：将海鲜壳进行热处理，然后加入有机胺前驱物的溶液，在常温条件下反应1h‑300h，得到混合液；将所述混合液离心提纯后真空干燥，然后进行碳化处理，再在0.5M‑3M的盐酸溶液中、在常温条件下处理1h‑10h，得到整体式介孔碳材料；其中，所述海鲜壳和有机胺前驱物的质量比为30：(4‑8)。
【技术特征摘要】
1.一种整体式介孔碳材料的制备方法，其包括以下步骤：将海鲜壳进行热处理，然后加入有机胺前驱物的溶液，在常温条件下反应1h-300h，得到混合液；将所述混合液离心提纯后真空干燥，然后进行碳化处理，再在0.5M-3M的盐酸溶液中、在常温条件下处理1h-10h，得到整体式介孔碳材料；其中，所述海鲜壳和有机胺前驱物的质量比为30：(4-8)。2.根据权利要求1所述的制备方法，其特征在于：所述海鲜壳包括蟹壳和/或虾壳。3.根据权利要求1所述的制备方法，其特征在于：所述有机胺前驱物包括多巴胺和/或二乙胺。4.根据权利要求1所述的制备方法，其特征在于：所述有机胺前驱物的溶液包括多巴胺和/或二乙胺的水溶液；优选地，所述有机胺前驱物的溶液的摩尔浓度为1mM-250mM。5.根据权利要求1所述的制备方法，其特征在于：所述热处理的温度为100℃-250℃，时间为1h-...
【专利技术属性】
技术研发人员：李鑫恒，吴丽琼，
申请(专利权)人：中国石油天然气股份有限公司，
类型：发明
国别省市：北京,11